DuPont Teijin Films Teijin® Tetoron® S Polyester Film, 150 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Teijin® Tetoron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Teijin® Tetoron® S Polyester Film, 150 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Teijin® Tetoron® S is the designation for a family of clear to hazy polyester films. They are general purpose films having good physical and electrical properties. They also have good chemical and thermal stability. These films are known for good roll formation and consistency of quality.The following Teijin® Tetoron® S film variants are available: S: Non-pretreatedSG: Low thermal shrinkageSG2: Low thermal shrinkage; Adhesion Pretreated (one side) SGZ: Release Liner (one side) SD: Adhesion Pretreated (one side) SP: Adhesion Pretreated (one side) SDW: Adhesion Pretreated (two side) SEW: Adhesion Pretreated (two side) PS: Sand blasted S film (matte)Typical Applications: Printing PlatesTracingFlexible Printed Circuits (FPC)Membrane Touch Switch (MTS)Information provided by DuPont.
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 140 %
140 %
ASTM D882A
Film Elongation at Break, TD 120 %
120 %
ASTM D882A
Coefficient of Friction, Dynamic 0.38
0.38
ASTM D1894
Coefficient of Friction, Static 0.34
0.34
ASTM D1894
Film Tensile Strength at Break, MD 254.93 MPa
36975 psi
ASTM D882A
Film Tensile Strength at Break, TD 264.93 MPa
38425 psi
ASTM D882A
Thermal Properties Metric English Comments
Shrinkage, MD 1.2 %

@Temperature 150 °C,
Time 1800 sec
1.2 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Shrinkage, TD 0.20 %

@Temperature 150 °C,
Time 1800 sec
0.20 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Optical Properties Metric English Comments
Haze 3.0 %
3.0 %
ASTM D1003