Bond Laminates TEPEX® dynalite 408-C200(2)-FG290(2)/45% Carbon – Filament Glass – TPU Consolidated Composite Laminate

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Carbon Fiber Reinforced
Manufacturer Bond Laminates
Trade Name TEPEX® dynalite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bond Laminates TEPEX® dynalite 408-C200(2)-FG290(2)/45% Carbon – Filament Glass – TPU Consolidated Composite Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Within the TEPEX® composite laminate, TPU distinguishes itself from alternative resin systems by its specific physical properties. The TPU resin is tough which results in an excellent impact and fatigue behavior and is easy to mold, obtaining an excellent surface quality. The TPU-carbon-glass laminates can easily be bonded with common adhesive systems. An excellent adhesion is achieved when overmolding with injection molding TPU grades.Typical application environments are within automotive applications, large structural parts, bumper systems, structural sporting goods applications, helmet shells.Information provided by Bond Laminates, GmbH.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
Filler Content 45 %
45 %
by volume
Thickness 1000 microns
39.4 mil
laminate layer thickness
Mechanical Properties Metric English Comments
Flexural Strength 705 MPa
102000 psi
longitudinal; ISO 178
705 MPa
102000 psi
transverse; ISO 178
Flexural Modulus 40.0 GPa
5800 ksi
transverse; ISO 178
40.5 GPa
5870 ksi
longitudinal; ISO 178
Thermal Properties Metric English Comments
Melting Point 190 °C
374 °F
DSC 3146
Maximum Service Temperature, Air 90.0 °C

@Time 7.20e+7 sec
194 °F

@Time 20000 hour
Relative Temperature Index; IEC 216/1
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
ISO 75-1/2
Minimum Service Temperature, Air -30.0 °C
-22.0 °F
Processing Properties Metric English Comments
Processing Temperature 210 - 230 °C
410 - 446 °F
Descriptive Properties Value Comments
Reinforcement Area weight
200 and 290 g/m²
Fabric
twill 2/2
Fibers
carbon and filament glass
Weight Rate
50% longitudinal and transverse
Yarn
3000/3x68 tex longitudinal and transverse