Lanxess Durethan® AKV 30 H3.0 000000 Nylon 66, 30% Glass Fibers

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 30 H3.0 000000 Nylon 66, 30% Glass Fibers.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 30% glass fibers, injection molding, heat-ageing stabilized
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ISO 1183
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Moisture Absorption at Equilibrium 1.9 %
1.9 %
50% RH; ISO 62
Water Absorption at Saturation 5.5 %
5.5 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm
 0.0040 in/in

@Thickness 0.0787 in
 Mold Temp 80°C; Melt Temp 300°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Thickness 2.00 mm
 0.011 in/in

@Thickness 0.0787 in
 Mold Temp 80°C; Melt Temp 300°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Ball Indentation Hardness 130 MPa
18900 psi
Conditioned; ISO 2039-1
230 MPa
33400 psi
ISO 2039-1
Tensile Strength at Break 115 MPa
16700 psi
Conditioned; ISO 527-1,-2
185 MPa
26800 psi
ISO 527-1,-2
Elongation at Break 3.5 %
3.5 %
ISO 527-1,-2
6.5 %
6.5 %
Conditioned; ISO 527-1,-2
Tensile Modulus 6.00 GPa
870 ksi
Conditioned; ISO 527-1,-2
9.50 GPa
1380 ksi
ISO 527-1,-2
Flexural Strength 185 MPa

@Strain 6.00 %
 26800 psi

@Strain 6.00 %
 Conditioned; ISO 178
280 MPa

@Strain 4.20 %
 40600 psi

@Strain 4.20 %
 ISO 178
Flexural Yield Strength 145 MPa

@Strain 3.50 %
 21000 psi

@Strain 3.50 %
 Conditioned
260 MPa

@Strain 3.50 %
 37700 psi

@Strain 3.50 %
Flexural Modulus 5.50 GPa
798 ksi
Conditioned; ISO 178
8.50 GPa
1230 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 180-1A
15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO) 55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 180-1U
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 180-1U
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179-1eU
7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
8.00 J/cm²

@Temperature 23.0 °C
 38.1 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179-1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179-1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179-1eA
Puncture Energy 1.90 J

@Load <=81.6 kg,
Temperature -30.0 °C
 1.40 ft-lb

@Load <=180 lb,
Temperature -22.0 °F
 ISO 6603-2
2.50 J

@Load <=102 kg,
Temperature 23.0 °C
 1.84 ft-lb

@Load <=225 lb,
Temperature 73.4 °F
 ISO 6603-2
4.20 J

@Load <=112 kg,
Temperature 23.0 °C
 3.10 ft-lb

@Load <=247 lb,
Temperature 73.4 °F
 Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1,-2
Melting Point 262 °C
504 °F
ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) >= 250 °C
>= 482 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75-1,-2
Deflection Temperature at 8.0 MPa 185 °C
365 °F
ISO 75-1,-2
Vicat Softening Point >= 230 °C

@Load 5.10 kg
 >= 446 °F

@Load 11.2 lb
 120°C/h; ISO 306
>= 230 °C

@Load 5.10 kg
 >= 446 °F

@Load 11.2 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Glow Wire Test 650 °C

@Diameter 0.800 mm
 1200 °F

@Diameter 0.0315 in
 IEC 60695-2-12
700 °C

@Diameter 1.60 mm
 1290 °F

@Diameter 0.0630 in
 IEC 60695-2-12
700 °C

@Diameter 3.00 mm
 1290 °F

@Diameter 0.118 in
 IEC 60695-2-12
Shrinkage 0.040 %

@Temperature 120 °C,
Time 14400 sec
 0.040 %

@Temperature 248 °F,
Time 4.00 hour
 Molding Post-shrinkage; ISO 294-4
0.10 %

@Temperature 120 °C,
Time 14400 sec
 0.10 %

@Temperature 248 °F,
Time 4.00 hour
 Molding Post-shrinkage; ISO 294-4
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 IEC 60250
4.5

@Frequency 100 Hz
 4.5

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 40.0 kV/mm

@Thickness 1.00 mm
 1020 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Dissipation Factor 0.010

@Frequency 100 Hz
 0.010

@Frequency 100 Hz
 IEC 60250
0.018

@Frequency 1.00e+6 Hz
 0.018

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 525 V
525 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 290 °C
554 °F
Processing conditions for test specimens; ISO 294
280 - 300 °C
536 - 572 °F
Recommended
Mold Temperature 80.0 °C
176 °F
Processing conditions for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Recommended
Drying Temperature 80.0 °C
176 °F