BNZ Materials Bazelite 2300 VLI Insulating Castable

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Bazelite
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials Bazelite 2300 VLI Insulating Castable.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blaz 2300 VLI is similar to Blaz 2300 but suitable for those applications where reducing conditions might be encountered. These high purity, low iron products are specifically designed for both back-up and exposed to furnace combustion.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0382 lb/in³	Fired at 5 hrs at 816°C

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.000550 GPa @Temperature 540 °C	0.0798 ksi @Temperature 1000 °F	Fired; ASTM C268
	0.000620 GPa @Temperature 815 °C	0.0899 ksi @Temperature 1500 °F	ASTM C268
	0.000620 GPa @Temperature 1095 °C	0.0899 ksi @Temperature 2003 °F	ASTM C268
	0.000970 GPa @Temperature 104 °C	0.141 ksi @Temperature 219 °F	Dried; ASTM C268
	0.000970 GPa @Temperature 1260 °C	0.141 ksi @Temperature 2300 °F	ASTM C268
Compressive Strength	2.14 MPa @Temperature 1095 °C	310 psi @Temperature 2003 °F	Cold Crush Strength
	2.55 MPa @Temperature 815 °C	370 psi @Temperature 1500 °F	Cold Crush Strength
	3.79 MPa @Temperature 1260 °C	550 psi @Temperature 2300 °F	Cold Crush Strength
	2.14 MPa @Treatment Temp. 540 °C	310 psi @Treatment Temp. 1000 °F	Cold Crush Strength; Dried 104°C
	4.14 MPa @Treatment Temp. 104 °C	600 psi @Treatment Temp. 219 °F	Cold Crush Strength; Dried 104°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	0.10 % @Temperature 540 °C	0.10 % @Temperature 1000 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 815 °C	0.20 % @Temperature 1500 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 1095 °C	0.20 % @Temperature 2003 °F	Permanent Linear Change; ASTM C210
	0.70 % @Temperature 1260 °C	0.70 % @Temperature 2300 °F	Permanent Linear Change; ASTM C210

Component Elements Properties	Metric	English	Comments
Al2O3	47.8 %	47.8 %
CaO	15.1 %	15.1 %
Fe2O3	0.50 %	0.50 %
Na2O	0.90 %	0.90 %	Includes K<sub>2</sub>O
SiO2	35 %	35 %
TiO2	1.0 %	1.0 %

Users viewing this material also viewed the following: