ArcelorMittal H 220 Solid solution steel, Cold rolled

Category	Metal , Ferrous Metal , Alloy Steel
Manufacturer	ArcelorMittal
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ArcelorMittal H 220 Solid solution steel, Cold rolled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Available in the following: uncoated (HC220P) and electrogalvanized (HC220P+ZE) Description: Solid solution steels are designed to provide high strength while maintaining good drawability. These steels are hardened by phosphorous in solid solution in the ferrite. Their combination of mechanical strength and drawability makes these grades suitable for numerous applications. They are particularly recommended for structural and reinforcement parts requiring good fatigue and impact strength (longitudinal beams, cross members, B-pillars, etc.). Solid solution steels are killed aluminum grades with lower drawing quality than the IF range of steels. The ArcelorMittal range of continuous hot dip galvanized (Extragal®/Galvannealed) steels is described under interstitial-free steels.Information provided by ArcelorMittal

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	340 - 400 MPa	49300 - 58000 psi
Tensile Strength, Yield	220 - 280 MPa	31900 - 40600 psi
Elongation at Break	>= 32 %	>= 32 %	L<Sub>0</sub>=80 mm, th<3 mm
Fatigue Strength	<= 275 MPa @# of Cycles 2.00e+6	<= 39900 psi @# of Cycles 2.00e+6
	<= 275 MPa @# of Cycles 1.00e+7	<= 39900 psi @# of Cycles 1.00e+7
	<= 295 MPa @# of Cycles 100000	<= 42800 psi @# of Cycles 100000

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.060 %	<= 0.060 %
Iron, Fe	>= 98.74 %	>= 98.74 %	as balance
Manganese, Mn	<= 0.70 %	<= 0.70 %
Silicon, Si	<= 0.50 %	<= 0.50 %