Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 200 kV/mm @Thickness 0.0508 mm |
5080 kV/in @Thickness 0.00200 in |
Amorphous Film; ASTM D149 |
Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire PEEK is produced to the highest industry standards and is characteriz.. |
|||
Dielectric Strength | 200 kV/mm @Thickness 0.500 mm |
5080 kV/in @Thickness 0.0197 in |
IEC 60243-1 |
Victrex® PEEK 450G General Purpose Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, standard flow, FDA food contac.. |
|||
Dielectric Strength | 200 kV/mm @Frequency 50.0 Hz, Temperature 150 °C |
5080 kV/in @Frequency 50.0 Hz, Temperature 302 °F |
ASTM D196-65 |
Isoflon Polyester film Polyethylene terephthalate film is a flexible film with high mechanical resistance. An excellent insulator, it preserves all its properties in a wide range of temperatures (-70°C to +150°C). .. |
|||
Dielectric Strength | 200 kV/mm @Thickness 0.0508 mm |
5080 kV/in @Thickness 0.00200 in |
Amorphous Film; ASTM D149 |
Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK) KetaSpire® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire® PEEK is produced to the highest industry standards and is cha.. |
|||
Dielectric Strength | 200 kV/mm @Thickness 0.0508 mm |
5080 kV/in @Thickness 0.00200 in |
Amorphous Film; ASTM D149 |
Solvay Specialty Polymers KetaSpire® KT-XXXX Polyetheretherketone (PEEK) KetaSpire® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire® PEEK is produced to the highest industry standards and is cha.. |
|||
Dielectric Strength | >= 200 kV/mm @Thickness 0.0254 mm |
>= 5080 kV/in @Thickness 0.00100 in |
ASTM D149 |
Solvay Specialty Polymers Radel® R-5000 Polyphenylsulfone (PPSU) Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins... |
|||
Dielectric Strength | >= 200 kV/mm @Thickness 0.0254 mm |
>= 5080 kV/in @Thickness 0.00100 in |
ASTM D149 |
Solvay Specialty Polymers Radel® R-5500 Polyphenylsulfone (PPSU) Radel® R-5500 is a general purpose extrusion grade of polyphenylsulfone (PPSU), offering exceptional hydrolytic stability and better toughness than most commercially available high-temperature po.. |
|||
Dielectric Strength | >= 200 kV/mm @Thickness 0.0254 mm |
>= 5080 kV/in @Thickness 0.00100 in |
ASTM D149 |
Solvay Specialty Polymers Radel® R-5600 Polyphenylsulfone (PPSU) Radel® R-5600 is a very high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer excep.. |
|||
Dielectric Strength | >= 200 kV/mm @Thickness 0.0254 mm |
>= 5080 kV/in @Thickness 0.00100 in |
ASTM D149 |
Solvay Specialty Polymers Radel® R-5800 Polyphenylsulfone (PPSU) Radel® R-5800 is a high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptiona.. |
|||
Dielectric Strength | 200 kV/mm @Thickness 0.130 mm |
5080 kV/in @Thickness 0.00512 in |
stepwise tension increase; ASTM D149-75 |
Arkema Group VOLTALEF® 300 HD PCTFE VOLTALEF® 300 HD is a chlorotrifluoroethylene powder. Used for compression molding, very good flow, non-flammable. Information provided by Arkema Group |
|||
Dielectric Strength | 200 kV/mm @Thickness 0.130 mm |
5080 kV/in @Thickness 0.00512 in |
stepwise tension increase; ASTM D149-75 |
Arkema Group VOLTALEF® 302 PCTFE VOLTALEF® 302 is a chlorotrifluoroethylene dense powder. Used in particular for compression molding, non-flammable. Information provided by Arkema Group |