Polymer Property : Dielectric Breakdown = 10000 V Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Breakdown	10000 V @Thickness 1.57 mm	10000 V @Thickness 0.0620 in	Cond D-48/50; ASTM D229 S/S
Industrial Laminates/Norplex NP630 Paper Base Laminate Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062", 0.125", and 0.500"
Dielectric Breakdown	10000 V @Thickness 1.57 mm	10000 V @Thickness 0.0620 in	Cond D-48/50; ASTM D229 S/S
Industrial Laminates/Norplex NP660 Paper Base Laminate Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500"
Dielectric Breakdown	10000 V @Thickness 1.57 mm	10000 V @Thickness 0.0620 in	Cond D-48/50; ASTM D229 S/S
Industrial Laminates/Norplex NP680 Paper Base Laminate Description: Hot punching grade with electrical properties between NP611 to NP631.Thickness Tested: 0.062", 0.125" & 0.500"
Dielectric Breakdown	10000 V @Thickness 1.57 mm	10000 V @Thickness 0.0620 in	Cond D-48/50; ASTM D229 S/S
Industrial Laminates/Norplex NP664 Paper Base Laminate Description: Low cost room temperature punching grade with mechanical and electrical properties similar to NP612. This version is made with pigment cover plies on the surface.Thickness Tested: 0.062..
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 20.0 sec	>= 10000 V @Temperature 194 °F, Time 0.00556 hour	Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe MF GC 21 Woven Glass Cloth Reinforced Melamine Resin - Round, Rolled Tube Used in mechanical and electrical applications. High mechanical strength. Good arc and tracking resistance. Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 60.0 sec	>= 10000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe MF GC 21 Woven Glass Cloth Reinforced Melamine Resin - Round, Rolled Tube Used in mechanical and electrical applications. High mechanical strength. Good arc and tracking resistance. Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 20.0 sec	>= 10000 V @Temperature 194 °F, Time 0.00556 hour	Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CC 22 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube Used in mechanical and electrical applications. Coarse weave (18-30 threads per cm).Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 60.0 sec	>= 10000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CC 22 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube Used in mechanical and electrical applications. Coarse weave (18-30 threads per cm).Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 20.0 sec	>= 10000 V @Temperature 194 °F, Time 0.00556 hour	Step -by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 42 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Good stability of electrical properties when exposed to high relative humidity. Lower mechanical and electrical properties than PF CP 41.Information..
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 60.0 sec	>= 10000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 42 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Good stability of electrical properties when exposed to high relative humidity. Lower mechanical and electrical properties than PF CP 41.Information..
Dielectric Breakdown	10000 V @Thickness 0.0508 mm	10000 V @Thickness 0.00200 in	ASTM D149
DuPont Teijin Films Melinex® ST507 Polyester Film Melinex® ST507 is a slightly hazy, heat stabilized, polyester film. It has good handling characteristics and is recommended for silver circuitry applications, particularly where an adhesion topcoat..
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 20.0 sec	>= 10000 V @Temperature 194 °F, Time 0.00556 hour	Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe EP GC 42 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at elevated temperatures. Very good stability of electrical properties when exposed to high relative ..
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 60.0 sec	>= 10000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe EP GC 42 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at elevated temperatures. Very good stability of electrical properties when exposed to high relative ..
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 20.0 sec	>= 10000 V @Temperature 194 °F, Time 0.00556 hour	Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 31 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in electrical and mechanical applications. Good stability of electrical properties when exposed to normal relative humidity.Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 60.0 sec	>= 10000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 31 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in electrical and mechanical applications. Good stability of electrical properties when exposed to normal relative humidity.Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 20.0 sec	>= 10000 V @Temperature 194 °F, Time 0.00556 hour	Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 43 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical applications and low-voltage electrical applications.Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Temperature 90.0 °C, Time 60.0 sec	>= 10000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 43 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical applications and low-voltage electrical applications.Information provided by Hippe.
Dielectric Breakdown	>= 10000 V @Thickness 0.500 mm	>= 10000 V @Thickness 0.0197 in	DIN EN 60243
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance) Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn..