Polymer Property : Electrical Resistivity = 0.00000430 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm
IBC Advanced Alloys BeralcastÂ® 363 Beryllium-Aluminum Alloy This alloy provides an ideal solution for weight, stiffness and thermal critical applications in aerospace, defense and commercial markets. BeAl-363 is a metal matrix composite which consists of 65%..
Electrical Resistivity	0.00000430 - 0.00000530 ohm-cm	0.00000430 - 0.00000530 ohm-cm	temper T651
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing ..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (5 hr)
CLAL-MSX SICLANIC S® TD4 Quenched Copper Alloy, 4/4 Hard SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (5 hr)
CLAL-MSX SICLANIC S® TF Quenched Copper Alloy, precipitation treated SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (4 hr)
CLAL-MSX SICLANIC S® TH3 Quenched Copper Alloy, 1/2 Hard, precipitation treated SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (4 hr)
CLAL-MSX SICLANIC S® TH4 Quenched Copper Alloy, 4/4 Hard, precipitation treated SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (5 hr)
CLAL-MSX SICLANIC S® TH4 Quenched Copper Alloy, 4/4 Hard, precipitation treated SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (5 hr)
CLAL-MSX SICLANIC S® TD3 Quenched Copper Alloy, 1/2 Hard SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm	precipitation hardened (1 hr)
CLAL-MSX SICLANIC S® TD3 Quenched Copper Alloy, 1/2 Hard SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm
Aleris Hokotol Aluminum Alloy, 200 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm
Aleris Hokotol Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm
Aleris Hokotol Aluminum Alloy, 300 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..
Electrical Resistivity	0.00000430 ohm-cm	0.00000430 ohm-cm
Aleris Hokotol Aluminum Alloy, 325 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..