CLAL-MSX SICLANIC S® TF Quenched Copper Alloy, precipitation treated

Category Metal , Nonferrous Metal , Copper Alloy
Manufacturer CLAL-MSX
Trade Name SICLANIC S®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CLAL-MSX SICLANIC S® TF Quenched Copper Alloy, precipitation treated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silvermechanicals properties on a par with those of copper cobalt- beryllium and of bronzeexcellent fatigue strengthvery competitive cost compared with copper-cobalt-beryllium.Information provided by CLAL-MSX
Physical Properties Metric English Comments
Density 8.90 g/cc
0.322 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers 170 - 190
170 - 190
150

@Time 3600 sec
150

@Time 1.00 hour
170

@Time 7200 sec
170

@Time 2.00 hour
180

@Time 10800 sec
180

@Time 3.00 hour
188

@Time 14400 sec
188

@Time 4.00 hour
191

@Time 18000 sec
191

@Time 5.00 hour
Tensile Strength, Ultimate 580 - 680 MPa
84100 - 98600 psi
Tensile Strength, Yield 450 - 550 MPa

@Strain 0.200 %
65300 - 79800 psi

@Strain 0.200 %
Elongation at Break 10 - 20 %
10 - 20 %
Modulus of Elasticity 130 GPa
18900 ksi
longitudinal
Flexural Strength >= 430 MPa
>= 62400 psi
Limit of elasticity in Bending
Fatigue Strength 245 MPa

@# of Cycles 1.00e+7
35500 psi

@# of Cycles 1.00e+7
Thermal Properties Metric English Comments
CTE, linear 19.0 µm/m-°C

@Temperature 20.0 - 300 °C
10.6 µin/in-°F

@Temperature 68.0 - 572 °F
Specific Heat Capacity 0.370 J/g-°C
0.0884 BTU/lb-°F
Thermal Conductivity 84.0 W/m-K
583 BTU-in/hr-ft²-°F
solid solution (or quenched) state
188.4 W/m-K
1307 BTU-in/hr-ft²-°F
quenched state
Melting Point 1040 - 1060 °C
1900 - 1940 °F
Solidus 1040 °C
1900 °F
Liquidus 1060 °C
1940 °F
Component Elements Properties Metric English Comments
Copper, Cu 96.9 %
96.9 %
Nickel, Ni 2.5 %
2.5 %
Silicon, Si 0.60 %
0.60 %
Electrical Properties Metric English Comments
Electrical Resistivity <= 0.00000400 ohm-cm
<= 0.00000400 ohm-cm
precipitation hardened
0.00000430 ohm-cm
0.00000430 ohm-cm
precipitation hardened (5 hr)
0.00000440 ohm-cm
0.00000440 ohm-cm
precipitation hardened (4 hr)
0.00000460 ohm-cm
0.00000460 ohm-cm
precipitation hardened (2 hr)
0.00000460 ohm-cm
0.00000460 ohm-cm
precipitation hardened (3 hr)
0.00000490 ohm-cm
0.00000490 ohm-cm
precipitation hardened (1 hr)
0.00000780 ohm-cm
0.00000780 ohm-cm
quenched