Aleris Hokotol Aluminum Alloy, 300 mm Thickness
| Category | Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy |
| Manufacturer | Aleris |
| Trade Name | Hokotol |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aleris Hokotol Aluminum Alloy, 300 mm Thickness.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; and mechanical components with elevated mechanical properties. Poor weldability and corrosion resistance. Very good machinability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.83 g/cc | 0.102 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 180 | 180 | |
| Hardness, Knoop | 232 | 232 | Estimated from Brinell |
| Hardness, Rockwell A | 59 | 59 | Estimated from Brinell |
| Hardness, Rockwell B | 96 | 96 | Estimated from Brinell |
| Hardness, Vickers | 217 | 217 | Estimated from Brinell |
| Tensile Strength, Ultimate | >= 460 MPa | >= 66700 psi | Minimum |
| 515 MPa | 74700 psi | Typical | |
| Tensile Strength, Yield | >= 400 MPa @Strain 0.200 % |
>= 58000 psi @Strain 0.200 % |
Minimum |
| 455 MPa @Strain 0.200 % |
66000 psi @Strain 0.200 % |
Typical | |
| Elongation at Break | >= 1.0 % | >= 1.0 % | Minimum |
| 2.0 % | 2.0 % | Typical | |
| Modulus of Elasticity | 70.3 GPa | 10200 ksi | |
| Machinability | 90 % | 90 % | |
| Shear Strength | 316 MPa | 45800 psi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.5 µm/m-°C @Temperature 20.0 - 100 °C |
13.1 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Thermal Conductivity | 154 W/m-K | 1070 BTU-in/hr-ft²-°F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 86 - 90.9 % | 86 - 90.9 % | as balance |
| Chromium, Cr | <= 0.10 % | <= 0.10 % | |
| Copper, Cu | 1.5 - 2.6 % | 1.5 - 2.6 % | |
| Iron, Fe | <= 0.30 % | <= 0.30 % | |
| Magnesium, Mg | 1.8 - 2.6 % | 1.8 - 2.6 % | |
| Manganese, Mn | <= 0.15 % | <= 0.15 % | |
| Other, total | <= 0.15 % | <= 0.15 % | |
| Silicon, Si | <= 0.20 % | <= 0.20 % | |
| Titanium, Ti | <= 0.060 % | <= 0.060 % | |
| Zinc, Zn | 5.7 - 7.6 % | 5.7 - 7.6 % | |
| Zirconium, Zr | 0.080 - 0.25 % | 0.080 - 0.25 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000430 ohm-cm | 0.00000430 ohm-cm |