BASF Ultradur® B 4300 G6 HR 30% Glass Filled BK 15116 PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultradur®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultradur® B 4300 G6 HR 30% Glass Filled BK 15116 PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: injection-molding grade with 30% glass-fibers; for rigid and dimensionally stable technical parts with increased requirements on hydrolysis resistance. For example automotive connectors and housings for electronic units under the hood.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.600 - 0.900 g/cc	0.0217 - 0.0325 lb/in³
Density	1.51 g/cc	0.0546 lb/in³	ISO 1183
Water Absorption	0.40 %	0.40 %	ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	ISO 62
Viscosity Measurement	108	108	[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow	0.0045 cm/cm	0.0045 in/in	ISO 2577
Linear Mold Shrinkage, Transverse	0.013 cm/cm	0.013 in/in	ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	ISO 527-1/-2
Elongation at Break	3.3 %	3.3 %	ISO 527-1/-2
Tensile Modulus	8.70 GPa	1260 ksi	ISO 527-1/-2
Charpy Impact Unnotched	7.00 J/cm² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	223 °C	433 °F	ISO 11357-1/-2
Maximum Service Temperature, Air	210 °C	410 °F
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	205 °C	401 °F	ISO 75-1/-2
Decomposition Temperature	>= 290 °C	>= 554 °F

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	250 °C	482 °F	Feeding zone
Zone 2	255 °C	491 °F	Compression
Zone 3	260 °C	500 °F	Metering-zone
Zone 4	260 °C	500 °F	Nozzle
Melt Temperature	260 °C	500 °F	Optimal
	250 - 275 °C	482 - 527 °F	Injection molding/Extrusion
Mold Temperature	60.0 - 100 °C	140 - 212 °F	Injection molding
	80.0 °C	176 °F	Optimal
Drying Temperature	80.0 - 120 °C	176 - 248 °F
Dry Time	4 hour	4 hour

Descriptive Properties	Value	Comments
Color	BK 15116
Commercial Status	Europe
Ignition Temperature	350°C	ASTM D1929
Peripheral screw speed	<0.25 m/s