Polymer Property : Thermal Conductivity = 199 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy plate, aged 1000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy plate, aged 4000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, plate, aged 1000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, plate, aged 1000 hours at 871Â°C (1600Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, plate, aged 4000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, plate, aged 4000 hours at 871Â°C (1600Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, plate, aged 8000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy, plate, aged 8000 hours at 871Â°C (1600Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	28.7 W/m-K @Temperature 1000 Â°C	199 BTU-in/hr-ftÂ²-Â°F @Temperature 1830 Â°F
Haynes HR-160Â® alloy plate, aged 8000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..