Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F)

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming and welding characteristics. Applications include a variety of fabricated components in municipal, industrial, hazardous, and nuclear waste heat recovery systems. Also suitable for utility boilers, sulfur plants, high-temperature furnaces, kilns, calciners, resource recovery units, cement kilns, pulp and paper recovery boilers, coal gasification systems, and fluidized-bed-combustion systems.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.08 g/cc
0.292 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 800 MPa
116000 psi
Tensile Strength, Yield 319 MPa

@Strain 0.200 %
46300 psi

@Strain 0.200 %
Elongation at Break 26 %
26 %
in 50.8 mm
Reduction of Area 19 %
19 %
Modulus of Elasticity 211 GPa
30600 ksi
RT
137 GPa

@Temperature 980 °C
19900 ksi

@Temperature 1800 °F
145 GPa

@Temperature 925 °C
21000 ksi

@Temperature 1700 °F
150 GPa

@Temperature 870 °C
21800 ksi

@Temperature 1600 °F
154 GPa

@Temperature 815 °C
22300 ksi

@Temperature 1500 °F
158 GPa

@Temperature 760 °C
22900 ksi

@Temperature 1400 °F
163 GPa

@Temperature 705 °C
23600 ksi

@Temperature 1300 °F
168 GPa

@Temperature 650 °C
24400 ksi

@Temperature 1200 °F
173 GPa

@Temperature 595 °C
25100 ksi

@Temperature 1100 °F
177 GPa

@Temperature 540 °C
25700 ksi

@Temperature 1000 °F
180 GPa

@Temperature 480 °C
26100 ksi

@Temperature 896 °F
183 GPa

@Temperature 425 °C
26500 ksi

@Temperature 797 °F
187 GPa

@Temperature 370 °C
27100 ksi

@Temperature 698 °F
192 GPa

@Temperature 315 °C
27800 ksi

@Temperature 599 °F
197 GPa

@Temperature 260 °C
28600 ksi

@Temperature 500 °F
201 GPa

@Temperature 205 °C
29200 ksi

@Temperature 401 °F
204 GPa

@Temperature 150 °C
29600 ksi

@Temperature 302 °F
208 GPa

@Temperature 90.0 °C
30200 ksi

@Temperature 194 °F
210 GPa

@Temperature 40.0 °C
30500 ksi

@Temperature 104 °F
Charpy Impact 20.0 J
14.8 ft-lb
aged 8000 hours at 760°C (1400°F)
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Temperature 25.0 - 95.0 °C
7.22 µin/in-°F

@Temperature 77.0 - 203 °F
13.7 µm/m-°C

@Temperature 25.0 - 205 °C
7.61 µin/in-°F

@Temperature 77.0 - 401 °F
14.0 µm/m-°C

@Temperature 25.0 - 315 °C
7.78 µin/in-°F

@Temperature 77.0 - 599 °F
14.4 µm/m-°C

@Temperature 25.0 - 425 °C
8.00 µin/in-°F

@Temperature 77.0 - 797 °F
14.9 µm/m-°C

@Temperature 25.0 - 540 °C
8.28 µin/in-°F

@Temperature 77.0 - 1000 °F
15.5 µm/m-°C

@Temperature 25.0 - 600 °C
8.61 µin/in-°F

@Temperature 77.0 - 1110 °F
15.7 µm/m-°C

@Temperature 25.0 - 700 °C
8.72 µin/in-°F

@Temperature 77.0 - 1290 °F
16.6 µm/m-°C

@Temperature 25.0 - 800 °C
9.22 µin/in-°F

@Temperature 77.0 - 1470 °F
17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Specific Heat Capacity 0.462 J/g-°C
0.110 BTU/lb-°F
RT
0.653 J/g-°C

@Temperature 700 °C
0.156 BTU/lb-°F

@Temperature 1290 °F
0.672 J/g-°C

@Temperature 800 °C
0.161 BTU/lb-°F

@Temperature 1470 °F
0.689 J/g-°C

@Temperature 900 °C
0.165 BTU/lb-°F

@Temperature 1650 °F
0.719 J/g-°C

@Temperature 1100 °C
0.172 BTU/lb-°F

@Temperature 2010 °F
0.732 J/g-°C

@Temperature 1200 °C
0.175 BTU/lb-°F

@Temperature 2190 °F
0.784 J/g-°C

@Temperature 1000 °C
0.187 BTU/lb-°F

@Temperature 1830 °F
Thermal Conductivity 10.9 W/m-K
75.6 BTU-in/hr-ft²-°F
RT
21.8 W/m-K

@Temperature 600 °C
151 BTU-in/hr-ft²-°F

@Temperature 1110 °F
24.7 W/m-K

@Temperature 700 °C
171 BTU-in/hr-ft²-°F

@Temperature 1290 °F
26.1 W/m-K

@Temperature 800 °C
181 BTU-in/hr-ft²-°F

@Temperature 1470 °F
26.9 W/m-K

@Temperature 900 °C
187 BTU-in/hr-ft²-°F

@Temperature 1650 °F
28.7 W/m-K

@Temperature 1000 °C
199 BTU-in/hr-ft²-°F

@Temperature 1830 °F
31.1 W/m-K

@Temperature 1100 °C
216 BTU-in/hr-ft²-°F

@Temperature 2010 °F
32.9 W/m-K

@Temperature 1200 °C
228 BTU-in/hr-ft²-°F

@Temperature 2190 °F
Melting Point 1293 - 1370 °C
2359 - 2500 °F
Solidus 1293 °C
2359 °F
Liquidus 1370 °C
2500 °F
Component Elements Properties Metric English Comments
Carbon, C 0.050 %
0.050 %
Chromium, Cr 28 %
28 %
Cobalt, Co 30 %
30 %
Iron, Fe <= 3.5 %
<= 3.5 %
Manganese, Mn 0.50 %
0.50 %
Molybdenum, Mo <= 1.0 %
<= 1.0 %
Nickel, Ni 37 %
37 %
Niobium, Nb (Columbium, Cb) <= 1.0 %
<= 1.0 %
Silicon, Si 2.75 %
2.75 %
Titanium, Ti 0.50 %
0.50 %
Tungsten, W <= 1.0 %
<= 1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001112 ohm-cm
0.0001112 ohm-cm
RT
0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
0.0001238 ohm-cm

@Temperature 800 °C
0.0001238 ohm-cm

@Temperature 1470 °F
0.0001245 ohm-cm

@Temperature 900 °C
0.0001245 ohm-cm

@Temperature 1650 °F
0.0001252 ohm-cm

@Temperature 1000 °C
0.0001252 ohm-cm

@Temperature 1830 °F
0.0001259 ohm-cm

@Temperature 1100 °C
0.0001259 ohm-cm

@Temperature 2010 °F
0.0001267 ohm-cm

@Temperature 1200 °C
0.0001267 ohm-cm

@Temperature 2190 °F