| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 20.5 W/m-K | 142 BTU-in/hr-ft²-°F | RT |
| Outokumpu 4713 High Temperature Ferritic Stainless Steel Does not form brittle phases but should only be exposed to moderately corrosive atmospheres due to low chromium content.Applications: Mostly used in high temperature applications with sulphurous atm.. |
|||
| Thermal Conductivity | 20.5 W/m-K @Temperature 500 °C |
142 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Thermal Conductivity | 20.5 W/m-K @Temperature 500 °C |
142 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 20.5 W/m-K @Temperature 100 °C |
142 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| CMT Materials METAPOR® HD 100 AL Air Permeable Material METAPOR® is a composite material made of aluminum granules and epoxy resin. The material is air-permeable over the entire surface due to its micro-porous structure allowing for unique design consi.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 20.4 W/m-K @Temperature 600 °C |
142 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||