- Outokumpu 4713 High Temperature Ferritic Stainless Steel
Outokumpu 4713 High Temperature Ferritic Stainless Steel
| Category | Metal , Ferrous Metal , Ferritic , Stainless Steel |
| Manufacturer | Outokumpu |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Outokumpu 4713 High Temperature Ferritic Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Does not form brittle phases but should only be exposed to moderately corrosive atmospheres due to low chromium content.Applications: Mostly used in high temperature applications with sulphurous atmospheres and/or low tensile loads such as for installations within: Chemical industry (drums)Power industry (coal burners)Metalworking industry (heat treatment boxes)Furnace technology (walls, doors)Available in hot rolled plate (Quarto) form.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.70 g/cc | 0.278 lb/in³ | RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 192 | 192 | RT; EN 10003-1 |
| Tensile Strength, Ultimate | 475 MPa | 68900 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Tensile Strength, Yield | 320 MPa @Strain 0.200 % |
46400 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| 350 MPa @Strain 1.00 % |
50800 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 | |
| Elongation at Break | 30 % | 30 % | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 600 °C |
7.33 µin/in-°F @Temperature 1110 °F |
|
| Specific Heat Capacity | 0.430 J/g-°C | 0.103 BTU/lb-°F | RT |
| Thermal Conductivity | 20.5 W/m-K | 142 BTU-in/hr-ft²-°F | RT |
| 25.4 W/m-K @Temperature 500 °C |
176 BTU-in/hr-ft²-°F @Temperature 932 °F |
||
| Maximum Service Temperature, Air | 800 °C | 1470 °F | Dry Air |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.50 % | 0.50 % | |
| Carbon, C | 0.12 % | 0.12 % | |
| Chromium, Cr | 7.0 % | 7.0 % | |
| Iron, Fe | 92.38 % | 92.38 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000710 ohm-cm | 0.0000710 ohm-cm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Annealing Temperature | 750 - 800 °C | 1380 - 1470 °F | Cooling: forced air or water |