Polymer Property : Thermal Conductivity = 141 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	20.3 W/m-K @Temperature 600 Â°C	141 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HastelloyÂ® N, 1.14 mm sheet, aged 10000 hours at 538Â°C (1000Â°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870Â°C (1300-1600Â°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity	20.3 W/m-K @Temperature 600 Â°C	141 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HastelloyÂ® N, 1.14 mm sheet, aged 10000 hours at 704Â°C (1300Â°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870Â°C (1300-1600Â°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity	20.3 W/m-K @Temperature 600 Â°C	141 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HastelloyÂ® N, 1.6 mm sheet, heat treated at 1175Â°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870Â°C (1300-1600Â°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity	20.3 W/m-K @Temperature 600 Â°C	141 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HastelloyÂ® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870Â°C (1300-1600Â°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity	20.3 W/m-K @Temperature 600 Â°C	141 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HastelloyÂ® N, weld metal, aged 500 hours at 649Â°C (1200Â°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870Â°C (1300-1600Â°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity	20.3 W/m-K	141 BTU-in/hr-ftÂ²-Â°F
Special Metals UDIMETÂ® Alloy 250 Maraging Steel A high-strength, maraging steel of iron and nickel with additions of molybdenum and titanium. It has the strength of standard 18Ni (250) maraging steel but the advantages of containing less molybde..
Thermal Conductivity	20.3 W/m-K @Temperature 600 °C	141 BTU-in/hr-ft²-°F @Temperature 1110 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity	20.3 W/m-K @Temperature 600 °C	141 BTU-in/hr-ft²-°F @Temperature 1110 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity	20.3 W/m-K @Temperature 600 °C	141 BTU-in/hr-ft²-°F @Temperature 1110 °F
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity	20.3 W/m-K @Temperature 600 °C	141 BTU-in/hr-ft²-°F @Temperature 1110 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity	20.3 W/m-K @Temperature 600 °C	141 BTU-in/hr-ft²-°F @Temperature 1110 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity	20.3 W/m-K @Temperature 600 °C	141 BTU-in/hr-ft²-°F @Temperature 1110 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity	20.3 W/m-K @Temperature 500 °C	141 BTU-in/hr-ft²-°F @Temperature 932 °F
Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a..