Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F)

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name Hastelloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.86 g/cc
0.320 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 812 MPa
118000 psi
674 MPa

@Temperature 538 °C
97800 psi

@Temperature 1000 °F
at 538°C after aging
Tensile Strength, Yield 311 MPa

@Strain 0.200 %
45100 psi

@Strain 0.200 %
Elongation at Break 50 %
50 %
in 50.8 mm
46 %

@Temperature 538 °C
46 %

@Temperature 1000 °F
in 50.8 mm at 538°C after aging
Modulus of Elasticity 122 GPa

@Temperature 1049 °C
17700 ksi

@Temperature 1920 °F
136 GPa

@Temperature 1000 °C
19700 ksi

@Temperature 1830 °F
143 GPa

@Temperature 954 °C
20700 ksi

@Temperature 1750 °F
151 GPa

@Temperature 904 °C
21900 ksi

@Temperature 1660 °F
157 GPa

@Temperature 854 °C
22800 ksi

@Temperature 1570 °F
163 GPa

@Temperature 800 °C
23600 ksi

@Temperature 1470 °F
171 GPa

@Temperature 700 °C
24800 ksi

@Temperature 1290 °F
181 GPa

@Temperature 577 °C
26300 ksi

@Temperature 1070 °F
181 GPa

@Temperature 632 °C
26300 ksi

@Temperature 1170 °F
187 GPa

@Temperature 500 °C
27100 ksi

@Temperature 932 °F
192 GPa

@Temperature 410 °C
27800 ksi

@Temperature 770 °F
202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
219 GPa

@Temperature 14.0 °C
31800 ksi

@Temperature 57.2 °F
Thermal Properties Metric English Comments
CTE, linear 12.3 µm/m-°C

@Temperature 21.0 - 316 °C
6.83 µin/in-°F

@Temperature 69.8 - 601 °F
12.7 µm/m-°C

@Temperature 21.0 - 427 °C
7.06 µin/in-°F

@Temperature 69.8 - 801 °F
13.4 µm/m-°C

@Temperature 21.0 - 538 °C
7.44 µin/in-°F

@Temperature 69.8 - 1000 °F
14.0 µm/m-°C

@Temperature 21.0 - 649 °C
7.78 µin/in-°F

@Temperature 69.8 - 1200 °F
14.7 µm/m-°C

@Temperature 21.0 - 760 °C
8.17 µin/in-°F

@Temperature 69.8 - 1400 °F
15.3 µm/m-°C

@Temperature 21.0 - 871 °C
8.50 µin/in-°F

@Temperature 69.8 - 1600 °F
15.8 µm/m-°C

@Temperature 21.0 - 982 °C
8.78 µin/in-°F

@Temperature 69.8 - 1800 °F
Specific Heat Capacity 0.419 J/g-°C

@Temperature 100 °C
0.100 BTU/lb-°F

@Temperature 212 °F
0.440 J/g-°C

@Temperature 200 °C
0.105 BTU/lb-°F

@Temperature 392 °F
0.456 J/g-°C

@Temperature 300 °C
0.109 BTU/lb-°F

@Temperature 572 °F
0.469 J/g-°C

@Temperature 400 °C
0.112 BTU/lb-°F

@Temperature 752 °F
0.477 J/g-°C

@Temperature 480 °C
0.114 BTU/lb-°F

@Temperature 896 °F
0.485 J/g-°C

@Temperature 540 °C
0.116 BTU/lb-°F

@Temperature 1000 °F
0.523 J/g-°C

@Temperature 570 °C
0.125 BTU/lb-°F

@Temperature 1060 °F
0.565 J/g-°C

@Temperature 590 °C
0.135 BTU/lb-°F

@Temperature 1090 °F
0.578 J/g-°C

@Temperature 680 °C
0.138 BTU/lb-°F

@Temperature 1260 °F
0.578 J/g-°C

@Temperature 700 °C
0.138 BTU/lb-°F

@Temperature 1290 °F
0.582 J/g-°C

@Temperature 660 °C
0.139 BTU/lb-°F

@Temperature 1220 °F
0.586 J/g-°C

@Temperature 620 °C
0.140 BTU/lb-°F

@Temperature 1150 °F
Thermal Conductivity 11.5 W/m-K
79.8 BTU-in/hr-ft²-°F
RT
13.1 W/m-K

@Temperature 100 °C
90.9 BTU-in/hr-ft²-°F

@Temperature 212 °F
13.1 W/m-K

@Temperature 200 °C
90.9 BTU-in/hr-ft²-°F

@Temperature 392 °F
14.4 W/m-K

@Temperature 300 °C
99.9 BTU-in/hr-ft²-°F

@Temperature 572 °F
16.5 W/m-K

@Temperature 400 °C
115 BTU-in/hr-ft²-°F

@Temperature 752 °F
18.0 W/m-K

@Temperature 500 °C
125 BTU-in/hr-ft²-°F

@Temperature 932 °F
20.3 W/m-K

@Temperature 600 °C
141 BTU-in/hr-ft²-°F

@Temperature 1110 °F
23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Melting Point 1300 - 1400 °C
2370 - 2550 °F
Solidus 1300 °C
2370 °F
Liquidus 1400 °C
2550 °F
Component Elements Properties Metric English Comments
Al + Ti <= 0.50 %
<= 0.50 %
Carbon, C <= 0.080 %
<= 0.080 %
Chromium, Cr 7.0 %
7.0 %
Cobalt, Co <= 0.20 %
<= 0.20 %
Copper, Cu <= 0.35 %
<= 0.35 %
Iron, Fe <= 5.0 %
<= 5.0 %
Manganese, Mn <= 0.80 %
<= 0.80 %
Molybdenum, Mo 16 %
16 %
Nickel, Ni 71 %
71 %
Silicon, Si <= 1.0 %
<= 1.0 %
Tungsten, W <= 0.50 %
<= 0.50 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000120 ohm-cm
0.000120 ohm-cm
RT
0.000124 ohm-cm

@Temperature 815 °C
0.000124 ohm-cm

@Temperature 1500 °F
0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F