Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® TPX-PPO/HIPS-02072 BK Availability: North AmericaForms: PelletsAdditive: PTFE LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and HomopolymerUL File Number: E157318Information provided by TP Composites,.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C @Thickness 3.17 mm |
207 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
Chase Plastics CP Pryme® A100HH ABS Molding Resin, High Heat Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 3501 Natural 1000 P Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 3501E Natural 1000 S Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | 0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
Diamond Polymers SE 3 HH Description: High Heat ABSInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | |
Aclo Accutech ABS ABS833G40L Glass Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | |
Aclo Accutech SAN SAN930G30L Glass Reinforced |