Diamond Polymers ABS 3501 Natural 1000 P

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ABS 3501 Natural 1000 P.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
ASTM D955
Melt Flow 0.30 g/10 min

@Load 5.00 kg,
Temperature 200 °C
0.30 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Procedure A Condition G; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 50.0 MPa
7250 psi
chs 2 in/min; ASTM D638
Flexural Modulus 2.65 GPa
385 ksi
Tangent, chs 0.05 in/min; ASTM D790
Izod Impact, Notched 3.20 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
6.00 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
bar; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648
97.2 °C
207 °F
0.125 in bar Annealed 4 hours at 80°C; ASTM D648
Vicat Softening Point 107 °C
224 °F
0.125 inch, 1 Kg; ASTM D1525
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Middle Barrel Temperature 190 - 250 °C
374 - 482 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Higher mold temperature provides a product with excellent surface finishing and less residual stress.
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 4.83 - 7.58 MPa
700 - 1100 psi