SABIC Innovative Plastics EXTEM UH1006 TPI Blend

Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Extem
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics EXTEM UH1006 TPI Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Resin is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
ASTM D792
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.39 %

@Time 86400 sec
0.39 %

@Time 24.0 hour
ISO 62-1
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ISO 62-4
Water Absorption at Saturation 2.1 %
2.1 %
ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
0.0080 - 0.010 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 6.60 kg,
Temperature 400 °C
10 g/10 min

@Load 14.6 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 112
112
ASTM D785
Tensile Strength at Break 107 MPa
15500 psi
5 mm/min; ISO 527
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength 68.0 MPa
9860 psi
ASTM D638
Tensile Strength, Yield 112 MPa
16200 psi
5 mm/min; ISO 527
120 MPa
17400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 19 %
19 %
5 mm/min; ISO 527
20 %
20 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 9.0 %
9.0 %
Type I, 5 mm/min; ASTM D638
9.0 %
9.0 %
5 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
3.80 GPa
551 ksi
5 mm/min; ASTM D638
Flexural Strength 109 MPa

@Temperature 150 °C
15800 psi

@Temperature 302 °F
ASTM D790
Flexural Yield Strength 155 MPa
22500 psi
2 mm/min; ISO 178
175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.00 GPa
435 ksi
2 mm/min; ISO 178
3.52 GPa
511 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.50 GPa

@Temperature 150 °C
363 ksi

@Temperature 302 °F
ASTM D790
Compressive Strength 160 MPa
23200 psi
SABIC Method
Izod Impact, Notched 0.750 J/cm
1.41 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 46.0 µm/m-°C

@Temperature 23.0 - 150 °C
25.6 µin/in-°F

@Temperature 73.4 - 302 °F
ASTM E 831
CTE, linear, Transverse to Flow 47.0 µm/m-°C

@Temperature 23.0 - 150 °C
26.1 µin/in-°F

@Temperature 73.4 - 302 °F
ASTM E 831
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 260 °C

@Thickness 3.20 mm
500 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 231 °C
448 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
238 °C

@Thickness 3.20 mm
460 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 257 °C
495 °F
Rate B/50; ASTM D1525
262 °C
504 °F
Rate B/50; ISO 306
262 °C
504 °F
Rate B/120; ISO 306
Oxygen Index 47 %
47 %
ISO 4589
Glow Wire Test 875 °C
1610 °F
IEC 60695-2-13
930 °C
1710 °F
IEC 60695-2-13
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Constant 3.5

@Frequency 1.00e+7 Hz
3.5

@Frequency 1.00e+7 Hz
ASTM D150
Dielectric Strength 54.0 kV/mm

@Thickness 0.800 mm
1370 kV/in

@Thickness 0.0315 in
in air; ASTM D149
Dissipation Factor 0.00050

@Frequency 1.00e+7 Hz
0.00050

@Frequency 1.00e+7 Hz
ASTM D150
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Draeger Tube Toxicity, Flaming (1.52mm) PASSES
AITM 3.0005, ABD0031
FAA Flammability, FAR 25.853 A/B PASSES
FAR 25.853
OSU total heat release (2 minute test) 0kW-min/m^2
FAR 25.853
OSU peak heat release rate (5 minute test) 21kW/m^2
FAR 25.853
Strength Retention after 1,000 hr aging in air at 240°C 88%
UL 746B
Strength Retention after 2,000 hr aging in air at 240°C 68%
UL 746B