Polymer Property : Deflection Temperature at 8.0 MPa = 392 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	180 - 200 °C	356 - 392 °F	Injection and Compression; ISO 75-C
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod..
Deflection Temperature at 8.0 MPa	180 - 200 °C	356 - 392 °F	Injection and Compression; ISO 75-C
Raschig Group EPOXIDUR® 3582 EP Epoxy Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Moldi..
Deflection Temperature at 8.0 MPa	180 - 200 °C	356 - 392 °F	ISO 75-C
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all..
Deflection Temperature at 8.0 MPa	120 - 200 °C	248 - 392 °F	Average value: 165 °C Grade Count:8
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled". Each property range of values repor..
Deflection Temperature at 8.0 MPa	100 - 200 °C	212 - 392 °F	Average value: 163 °C Grade Count:11
Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values..