Polymer Property : Deflection Temperature at 8.0 MPa = 100 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	100 - 120 °C	212 - 248 °F	Injection; ISO 75-C
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Deflection Temperature at 8.0 MPa	100 - 120 °C	212 - 248 °F	Injection; ISO 75-C
Raschig Group 3536 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
Deflection Temperature at 8.0 MPa	100 - 120 °C	212 - 248 °F	ISO 75-C
Raschig Group DECAL® 2061 Phenolic Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and ..
Deflection Temperature at 8.0 MPa	100 - 120 °C	212 - 248 °F	ISO 75-C
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/..
Deflection Temperature at 8.0 MPa	>= 100 °C	>= 212 °F	ISO 175
Perstorp Compounds AMITEC VXO UF/MF blend A special Urea Formaldehyde/Melamine Formaldehyde blend that enhances surface properties and is optimized for cost-effective injection molding of visible components.Information provided by Perstorp ..
Deflection Temperature at 8.0 MPa	100 °C	212 °F	ISO 75-1/-2
Lanxess Pocan® T 7331 POS151 000000 PBT + PET, 30% Glass Fiber (discontinued **) PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Deflection Temperature at 8.0 MPa	100 - 120 °C	212 - 248 °F	ISO 75-C
Raschig Group 3572 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength and electrical strength, enhanced elasticity for ensuring good sealing under extreme heat and/or humidity, good chemical resis..
Deflection Temperature at 8.0 MPa	100 - 160 °C	212 - 320 °F	Average value: 128 °C Grade Count:3
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of ..
Deflection Temperature at 8.0 MPa	100 Â°C	212 Â°F	ISO 75-1/-2
Lanxess PocanÂ® T 7331 000000 PBT + PET, 30% Glass Fiber PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load
Deflection Temperature at 8.0 MPa	100 °C	212 °F	ISO 75-1/-2
EMS-Grivory Grivory® HT2V-15H PA6T/66-GF15 Product description: Grivory HT2V-15H is a 15 % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation acc. to ISO..
Deflection Temperature at 8.0 MPa	100 °C	212 °F	ISO 75-1/-2
EMS-Grivory Grivory® HT2VZ-15H PA6T/66-GF15 Information provided by EMS Grivory
Deflection Temperature at 8.0 MPa	100 °C	212 °F	ISO 75-1/-2
EMS-Grivory Grivory® TSGZ-30 PA666-GF30 Product description: Grilon TSGZ-30 is a heat stabilized, normal viscosity, and impact modified PA66 + PA6 injection molding grade with 30% glass fibers. Grilon TSGZ-30 has the following important p..
Deflection Temperature at 8.0 MPa	100 - 200 °C	212 - 392 °F	Average value: 163 °C Grade Count:11
Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values..
Deflection Temperature at 8.0 MPa	100 °C	212 °F	ISO 75-1/-2
EMS-Grivory Grivory® LC-15H black PA12-CF15 Product description: Grilamid LC-15H black is a Polyamide 12 injection molding product reinforced with 15% carbon fibers. The product is inherently black and is only available in this color.Main Att..