Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition O Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6 Heat Treatment Condition T6 (Quench in water at RT)abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of p.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T6 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T4 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6 PM cast Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 20.0 - 900 °C |
9.06 µin/in-°F @Temperature 68.0 - 1650 °F |
|
Haynes Hastelloy® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 21.0 - 927 °C |
9.06 µin/in-°F @Temperature 69.8 - 1700 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 21.0 - 927 °C |
9.06 µin/in-°F @Temperature 69.8 - 1700 °F |
|
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 21.0 - 927 °C |
9.06 µin/in-°F @Temperature 69.8 - 1700 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 21.0 - 927 °C |
9.06 µin/in-°F @Temperature 69.8 - 1700 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 21.0 - 927 °C |
9.06 µin/in-°F @Temperature 69.8 - 1700 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 25.0 - 800 °C |
9.06 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 500 °C |
9.06 µin/in-°F @Temperature 32.0 - 932 °F |
|
CLAL-MSX CUPROROR® TL1 1/4 hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 500 °C |
9.06 µin/in-°F @Temperature 32.0 - 932 °F |
|
CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 500 °C |
9.06 µin/in-°F @Temperature 32.0 - 932 °F |
|
CLAL-MSX CUPROROR® TL5 Spring, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 500 °C |
9.06 µin/in-°F @Temperature 32.0 - 932 °F |
|
CLAL-MSX CUPROROR® TL4 Hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 21.0 - 927 °C |
9.06 µin/in-°F @Temperature 69.8 - 1700 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |
|||
CTE, linear | 16.3 µm/m-°C @Temperature 0.000 - 800 °C |
9.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |