PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T6

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Property data for Heat Treatment Condition T6 (Quenching in water at RT).Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.622 - 2.898 g/cc
0.09473 - 0.1047 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 210
>= 210
HV30
Tensile Strength at Break >= 190 MPa

@Temperature 300 °C
>= 27600 psi

@Temperature 572 °F
>= 290 MPa

@Temperature 250 °C
>= 42100 psi

@Temperature 482 °F
>= 481 MPa

@Temperature 20.0 °C
>= 69800 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 119 MPa

@Temperature 300 °C
>= 17300 psi

@Temperature 572 °F
>= 238 MPa

@Temperature 250 °C
>= 34500 psi

@Temperature 482 °F
>= 478 MPa

@Temperature 20.0 °C
>= 69300 psi

@Temperature 68.0 °F
Elongation at Break >= 0.13 %

@Temperature 20.0 °C
>= 0.13 %

@Temperature 68.0 °F
>= 1.0 %

@Temperature 250 °C
>= 1.0 %

@Temperature 482 °F
>= 2.7 %

@Temperature 300 °C
>= 2.7 %

@Temperature 572 °F
Modulus of Elasticity >= 73.0 GPa

@Temperature 300 °C
>= 10600 ksi

@Temperature 572 °F
>= 81.0 GPa

@Temperature 250 °C
>= 11700 ksi

@Temperature 482 °F
>= 96.0 GPa

@Temperature 20.0 °C
>= 13900 ksi

@Temperature 68.0 °F
Poissons Ratio 0.286

@Temperature 20.0 °C
0.286

@Temperature 68.0 °F
Condition F
0.289

@Temperature 100 °C
0.289

@Temperature 212 °F
Condition F
0.29

@Temperature 150 °C
0.29

@Temperature 302 °F
Condition F
0.291

@Temperature 200 °C
0.291

@Temperature 392 °F
Condition F
0.294

@Temperature 250 °C
0.294

@Temperature 482 °F
Condition F
0.294

@Temperature 300 °C
0.294

@Temperature 572 °F
Condition F
Fatigue Strength 241.6 MPa

@Temperature 20.0 °C
35040 psi

@Temperature 68.0 °F
P50% rotary bending values for 5X10<sup>7</sup> cycles
Thermal Properties Metric English Comments
CTE, linear 15.3 - 16.3 µm/m-°C

@Temperature 20.0 - 100 °C
8.50 - 9.06 µin/in-°F

@Temperature 68.0 - 212 °F
16.1 - 17.1 µm/m-°C

@Temperature 20.0 - 200 °C
8.94 - 9.50 µin/in-°F

@Temperature 68.0 - 392 °F
17.0 - 18.0 µm/m-°C

@Temperature 20.0 - 300 °C
9.44 - 10.0 µin/in-°F

@Temperature 68.0 - 572 °F
Specific Heat Capacity 0.840 - 0.880 J/g-°C
0.201 - 0.210 BTU/lb-°F
Thermal Conductivity 95.30 W/m-K

@Temperature 400 °C
661.4 BTU-in/hr-ft²-°F

@Temperature 752 °F
99.20 W/m-K

@Temperature 200 °C
688.4 BTU-in/hr-ft²-°F

@Temperature 392 °F
99.20 W/m-K

@Temperature 300 °C
688.4 BTU-in/hr-ft²-°F

@Temperature 572 °F
99.60 W/m-K

@Temperature 100 °C
691.2 BTU-in/hr-ft²-°F

@Temperature 212 °F
101.2 W/m-K

@Temperature 30.0 °C
702.3 BTU-in/hr-ft²-°F

@Temperature 86.0 °F
Melting Point 528 - 784 °C
982 - 1440 °F
Solidus 528.1 - 534.1 °C
982.6 - 993.4 °F
Liquidus 784.2 - 790.2 °C
1444 - 1454 °F
Component Elements Properties Metric English Comments
Aluminum, Al 63 %
63 %
As Balance
Cobalt, Co 1.0 %
1.0 %
Copper, Cu 3.0 %
3.0 %
Iron, Fe 3.0 %
3.0 %
Magnesium, Mg 1.0 %
1.0 %
Nickel, Ni 3.0 %
3.0 %
Silicon, Si 25 %
25 %
Titanium, Ti 1.0 %
1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000910 - 0.0000100 ohm-cm
0.00000910 - 0.0000100 ohm-cm