- Polymer Property : CTE, linear = 13.8 µm/m-°C
Polymer Property : CTE, linear = 13.8 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.8 µm/m-°C @Temperature 0.000 - 300 °C |
7.67 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® 6K 12.7 or 22.2 mm plate 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 0.000 - 500 °C |
7.67 µin/in-°F @Temperature 32.0 - 932 °F |
|
| Kennametal Stellite Stellite® 12 PM cast Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 300 °C |
7.67 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 23.0 - 500 °C |
7.67 µin/in-°F @Temperature 73.4 - 932 °F |
|
| ATI Allegheny Ludlum Alloy 255 Stainless Steel, UNS S32550 Alloy 255 is a 25% chromium duplex ferritic-austenitic stainless steel designed to provide a superior combination of high strength and excellent corrosion resistance for a wide variety of applicatio.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 13.8 µm/m-°C @Temperature 25.0 - 400 °C |
7.67 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||