- Polymer Property : Glass Transition Temp, Tg = 145 °C
Polymer Property : Glass Transition Temp, Tg = 145 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 145 °C | 293 °F | ASTM D3418 |
| Quadrant EPP Quadrant PC 1000 Extruded, Unfilled, Polycarbonate (ASTM Product Data Sheet) |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | |
| Covestro Makrolon® CD 2005 Polycarbonate, Optical/Compact Disc Grade
(discontinued **) Injection molding grade with exceptionally good flow, for optical storage media such as CD.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | |
| Cookson Group Plaskon® 2929BNSC Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound for the encapsulation of semiconductor devices and fiber optics. Excellent moldability (good release, .. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | Tg |
| Industrial Laminates/Norplex NP180 Synthetic Fabric
(discontinued **) Description: aramid fabric material with a high performance epoxy resin matrix. Excellent electrical and mechanical properties at elevated temperatures and in adverse environments.Thickness Tested: .. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | DMA, ASTM D4065 |
| Quantum Composites QC-8100 60% Glass Fiber Vinyl Ester SMC
(discontinued **) QC-8100 is a vinyl ester based sheet molding compound (SMC) designed for compression molding of components requiring high structural strength and corrosion resistance. Form and Colors = Rolled Shee.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | MCI Method |
| Mitsui APELâ„¢ APL6015T Cyclo Olefin Copolymer (COC) This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt proces.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | |
| Covestro Makrolon® 2205 Polycarbonate, Injection Grade Exceptionally good flow injection molding grade with easy mold release, for parts with a low wall thickness and long flow paths.Information provided by Bayer.As of 1 September 2015, Bayer MaterialSc.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | 10°C/min; ISO 11357-1,-2 |
| Covestro Makrolon® 2256 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 2556 Polycarbonate MVR (300 °C/1.2 kg) 14 cm3/10 minEasy releaseGood hydrolysis resistanceInjection moldingAvailable in transparentTranslucent and opaque colorsFood contact gradePreprocessingMax. Water content |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 2558 Polycarbonate ISO 7391-PC,MR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minMedical devicessuitable for ETO and steam sterilization at 121 °CComplies with the requirements of FDA-modified ISO 10993-1 and USP Class.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 2656 Polycarbonate ISO 7391-PC,MR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minFood contact qualityMedium viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAv.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 2856 Polycarbonate ISO 7391-PC,MR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 9.5 cm3/10 minFood contact qualityMedium viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAva.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 3107 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minGeneral purposeHigh viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transpare.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 6455 Polycarbonate, Flame Retardant Grade MVR (300 °C/1.2 kg) 12.5 cm3/10 minUL 94V-0/3.0 mmeasy releaseinjection moldingavailable in transparenttranslucent and opaque colorsPreprocessingMax. Water content |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® DP1-1821* Polycarbonate Developmental productMVR (300 °C/1.2 kg) 6.0 cm3/10 minHigh viscosityUV stabilizedEasy releaseInjection moldingAvailable in colorless transparent onlyPreprocessingMax. Water content |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | 10°C/min; ISO 11357-1,-2 |
| Covestro Makrolon® FU4007 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Furniture applications.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® LQ3147 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minOptical lensHigh viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in clear tints .. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | dynamic; DIN 53 736 |
| Hippe PC Polycarbonate Hard, stiff, very good impact properties with a wide range of temperature (to -100°C). High stability of shape under heat. Clear with own slight yellowish color. Low water absorption, weather-re.. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | ISO 11357-1/-2 |
| Covestro Makrolon® 1243 Polycarbonate ISO 7391-PC,ELS,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityBranchedUV stabilizedEasy releaseAvailable in color code 550111onlyMulti wall sheet/profilesPreprocessi.. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Comtuf® 410 Polycarbonate/Polyester Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Comtuf® 520 Polycarbonate/Styrenic Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Comtuf® 523 Polycarbonate/Styrenic Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Hiloy® 511 Polycarbonate, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.10% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Hiloy® 512 Polycarbonate, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Hiloy® 516 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Hiloy® 517 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Lubrilon® 512 Polycarbonate, Glass Fiber/PTFE, UL Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Comtuf® 413 Glass Reinforced, Polycarbonate/Polyester Alloy, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| A. Schulman ComAlloy Hiloy® 518 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Glass Transition Temp, Tg | 145 °C | 293 °F | DSC |
| Gharda Chemicals GATONE™ 5300PF Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||