Polymer Property : CTE, linear, Parallel to Flow = 75.6 Âµin/in-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	136 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	75.6 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
SABIC Innovative Plastics LNP THERMOCOMP HX03409C PA11 LNP* THERMOCOMP* HX03409C is a compound based on Nylon 11 resin containing Proprietary Filler(s). Added features of this material include: Clean Compound System, High Specific Gravity.
CTE, linear, Parallel to Flow	136 µm/m-°C @Temperature 23.0 - 200 °C	75.6 µin/in-°F @Temperature 73.4 - 392 °F	ASTM D696
Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures..
CTE, linear, Parallel to Flow	136 µm/m-°C @Temperature 23.0 - 200 °C	75.6 µin/in-°F @Temperature 73.4 - 392 °F	ASTM D696
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature..
CTE, linear, Parallel to Flow	136 µm/m-°C @Temperature 23.0 - 200 °C	75.6 µin/in-°F @Temperature 73.4 - 392 °F	ASTM D696
Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures..
CTE, linear, Parallel to Flow	136 µm/m-°C @Temperature 23.0 - 200 °C	75.6 µin/in-°F @Temperature 73.4 - 392 °F	ASTM D696
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature..