Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 60.0 °C |
75.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP HX03409C PA11 LNP* THERMOCOMP* HX03409C is a compound based on Nylon 11 resin containing Proprietary Filler(s). Added features of this material include: Clean Compound System, High Specific Gravity. |
|||
CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 200 °C |
75.6 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures.. |
|||
CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 200 °C |
75.6 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |
|||
CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 200 °C |
75.6 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
Dalau Dalcon 006 75% Virgin PTFE, 25% Glass Fiber Applications & Industries:General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperatures.. |
|||
CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 200 °C |
75.6 µin/in-°F @Temperature 73.4 - 392 °F |
ASTM D696 |
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |