SABIC Innovative Plastics LNP THERMOCOMP HX03409C PA11

Category Polymer , Thermoplastic , Nylon , Nylon 11
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP HX03409C PA11.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* HX03409C is a compound based on Nylon 11 resin containing Proprietary Filler(s). Added features of this material include: Clean Compound System, High Specific Gravity.
Physical Properties Metric English Comments
Density 2.24 g/cc
0.0809 lb/in³
ISO 1183
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ISO 62-1
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 33.0 MPa
4790 psi
50 mm/min; ISO 527
Elongation at Break 42 %
42 %
50 mm/min; ISO 527
Tensile Modulus 1.50 GPa
218 ksi
1 mm/min; ISO 527
Flexural Yield Strength 51.0 MPa
7400 psi
2 mm/min; ISO 178
Flexural Modulus 1.90 GPa
276 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 75.0 kJ/m²
35.7 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 136 µm/m-°C

@Temperature 23.0 - 60.0 °C
75.6 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 110 µm/m-°C

@Temperature 23.0 - 60.0 °C
61.1 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 146 °C
295 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af