Polymer Property : Flexural Strength = 36300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	250 MPa @Temperature 23.0 °C	36300 psi @Temperature 73.4 °F	ISO 178
Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 20% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food conta..
Flexural Strength	250 MPa @Temperature 23.0 °C	36300 psi @Temperature 73.4 °F	ISO 178
Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black Product Description: High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, Standard viscos..
Flexural Strength	250 MPa @Temperature 125 °C	36300 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, FDA food contact compliant..
Flexural Strength	250 MPa @Strain 3.00 %	36300 psi @Strain 3.00 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced PA 66, 40% glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warpInformation provided by LANXESS.
Flexural Strength	250 MPa @Strain 4.30 %	36300 psi @Strain 4.30 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 130 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength	250 MPa @Strain 3.70 %	36300 psi @Strain 3.70 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber PA 6, 35% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS.
Flexural Strength	250 MPa @Temperature -40.0 °C	36300 psi @Temperature -40.0 °F	Practical Use (Water Absorption 1.7%); ASTM-D790
Toyobo GLAMIDE® T-602G30 MXD66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	250 MPa @Temperature -40.0 °C	36300 psi @Temperature -40.0 °F	Practical Use; ASTM-D790
Toyobo GLAMIDE® T-669VGB Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	250 MPa @Temperature 23.0 °C	36300 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-791HT 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	250 MPa @Thickness >=20.0 mm	36300 psi @Thickness >=0.787 in	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope..
Flexural Strength	250 MPa @Thickness >=1.50 mm	36300 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope..
Flexural Strength	250 MPa @Thickness >=1.50 mm	36300 psi @Thickness >=0.0591 in	1hr/130°C/measured at 130°C; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax EP 10 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets Description: High mechanical strength at elevated temperatures. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. Can be used at c..