Toyobo GLAMIDE® TY-791HT 6T-Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-791HT 6T-Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-791HT is a GF/mineral reinforced, aromatic 6T-Nylon with high rigidity and good weather resistance. It also has a good finish of coating.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 60 % | 60 % | |
| Water Absorption | 0.60 % | 0.60 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Thickness 1.00 mm |
0.0010 - 0.0020 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0020 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0020 - 0.0050 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 77.0 MPa @Temperature 80.0 °C |
11200 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.4%); ASTM-D638 |
| 97.0 MPa @Temperature 80.0 °C |
14100 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 134 MPa @Temperature 23.0 °C |
19400 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.4%); ASTM-D638 | |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 195 MPa @Temperature -40.0 °C |
28300 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.4%); ASTM-D638 | |
| 220 MPa @Temperature -40.0 °C |
31900 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 1.3 % | 1.3 % | ASTM-D638 |
| Flexural Strength | 112 MPa @Temperature 80.0 °C |
16200 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.4%); ASTM-D790 |
| 135 MPa @Temperature 80.0 °C |
19600 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 210 MPa @Temperature 23.0 °C |
30500 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.4%); ASTM-D790 | |
| 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 280 MPa @Temperature -40.0 °C |
40600 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.4%); ASTM-D790 | |
| 305 MPa @Temperature -40.0 °C |
44200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 7.30 GPa @Temperature 80.0 °C |
1060 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.4%); ASTM-D790 |
| 8.80 GPa @Temperature 80.0 °C |
1280 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 17.8 GPa @Temperature 23.0 °C |
2580 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.4%); ASTM-D790 | |
| 18.5 GPa @Temperature -40.0 °C |
2680 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.4%); ASTM-D790 | |
| 18.5 GPa @Temperature 23.0 °C |
2680 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 19.0 GPa @Temperature -40.0 °C |
2760 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.650 J/cm @Temperature -40.0 °C |
1.22 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.4%); ASTM-D256 | |
| 0.750 J/cm @Temperature 23.0 °C |
1.41 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.4%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | Practical Use (Water Absorption 1.4%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.4%); ASTM-D149 |
| 28.0 kV/mm @Thickness 2.00 mm |
711 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Injection Pressure | 50.0 - 90.0 MPa | 7250 - 13100 psi |
Users viewing this material also viewed the following:
- Ineos Nova 50 High Performance Styrenic Enhanced Polystyrene (discontinued **)
- Lehmann & Voss LUVOCOM® 50/CF/10/TF/15/BK 100 Polycarbonate, with carbon fiber and PTFE
- Lehmann & Voss LUVOCOM® 1105-8402 PEEK, with glass fiber
- Saint-Gobain Chemlam® Silver 12 Wear Resistant Industrial Laminate
- Saint-Gobain Tygon® Transflow S3™ Vacuum Phthalate-free Vacuum and Dairy Tubing, A-24 and A24-C
- A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- EMS-Grivory Grivory® HTV-3H1 black 9205 PA6T/6I-GF30
- Daikin NEOFLON EC-6520 ETFE Coating Powder, White
- Carpenter Extendo-Die® Hot Work Die Steel, Tempered 560°C
- Asahi Kasei Thermylene® P6-25FG-0687 25% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved