Lanxess Durethan® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 35% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.358 g/cc | 1.358 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm | 0.00050 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0022 cm/cm | 0.0022 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0014 cm/cm | 0.0014 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0058 cm/cm | 0.0058 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 104 MPa | 15100 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 165 MPa | 23900 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 2.9 % | 2.9 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 5.1 % | 5.1 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 6.30 GPa | 914 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 9.50 GPa | 1380 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 160 MPa @Strain 5.10 % |
23200 psi @Strain 5.10 % |
cond., 2 mm/min; ISO 178-A |
| 250 MPa @Strain 3.70 % |
36300 psi @Strain 3.70 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 140 MPa @Strain 3.50 % |
20300 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 250 MPa @Strain 3.50 % |
36300 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 5.70 GPa | 827 ksi | cond., 2 mm/min; ISO 178-A |
| 8.70 GPa | 1260 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| 19.0 kJ/m² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | cond.; ISO 180-1U |
| 75.0 kJ/m² | 35.7 ft-lb/in² | d.a.m.; ISO 180-1U | |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | d.a.m.; ISO 179-1eU |
| 8.00 J/cm² | 38.1 ft-lb/in² | cond.; ISO 179-1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| 270 °C | 518 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability Test | passed | ISO 3795; US-FMVSS302 |
| ISO Shortname | ISO 1874 PA 6, GR, 10-090, GF35 |