Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.84 - 10.8 GPa | 992 - 1570 ksi | Average value: 9.34 GPa Grade Count:8 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Flexural Modulus | 6.84 GPa | 992 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RX05496 PA 66 LNP* LUBRICOMP* RX05496 is a compound based on Nylon 66 resin containing 30% Mixed Glass, 15% PTFE, Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 6.84 GPa | 992 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RX05496 PA 66 (Asia Pacific) LNP* Lubricomp* RX05496 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 6.84 GPa | 992 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare. |
|||
Flexural Modulus | 6.84 GPa | 992 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON DE003M PC LNP* STAT-KON* DE003M is a compound based on Polycarbonate containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
Flexural Modulus | 6.84 GPa | 992 ksi | ASTM D790 |
Aaron Industries AAROPRENE® GFABS 4040 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |