Polymer Property : Flexural Modulus = 1565 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	10.79 GPa	1565 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber.
Flexural Modulus	10.79 GPa	1565 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10 LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber.
Flexural Modulus	10.79 GPa	1565 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp QF008R PA 6/10 LNP* Thermocomp* QF008R is a compound based on Nylon 6/10 containing Glass Fiber. Characteristics of this grade are: Easy Release.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus	10.79 GPa	1565 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
Flexural Modulus	10.79 GPa	1565 ksi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON LX04420C PEEK LNP* STAT-KON* LX04420C is a compound based on Polyetheretherketone resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding Syst..
Flexural Modulus	10.79 GPa	1565 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci..