SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D 792
1.42 g/cc
0.0513 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.090 %
0.090 %
23°C / 50% RH; ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 171 MPa
24800 psi
ASTM D 638
183 MPa
26500 psi
ISO 527
Elongation at Break 3.3 %
3.3 %
ASTM D 638
Tensile Modulus 12.42 GPa
1801 ksi
50 mm/min; ASTM D 638
Flexural Strength 255 MPa
37000 psi
ASTM D 790
Flexural Modulus 10.78 GPa
1564 ksi
ISO 178
10.79 GPa
1565 ksi
ASTM D 790
Izod Impact, Notched 1.33 J/cm

@Temperature 23.0 °C
2.49 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 11.1 J/cm

@Temperature 23.0 °C
20.8 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 219 °C

@Thickness 3.20 mm
426 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D 648