SABIC Innovative Plastics LNP STAT-KON LX04420C PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON LX04420C PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* LX04420C is a compound based on Polyetheretherketone resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ASTM D792
1.36 g/cc
0.0491 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ASTM D955
0.0034 cm/cm

@Time 86400 sec
 0.0034 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0060 cm/cm

@Time 86400 sec
 0.0060 in/in

@Time 24.0 hour
 ASTM D955
0.0062 cm/cm

@Time 86400 sec
 0.0062 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
149 MPa
21600 psi
ISO 527
Tensile Strength, Yield 149 MPa
21600 psi
ASTM D638
149 MPa
21600 psi
ISO 527
Elongation at Break 2.1 %
2.1 %
ISO 527
2.3 %
2.3 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ISO 527
2.3 %
2.3 %
ASTM D638
Tensile Modulus 11.5 GPa
1670 ksi
1 mm/min; ISO 527
11.99 GPa
1739 ksi
50 mm/min; ASTM D638
Flexural Strength 241 MPa
35000 psi
ASTM D790
241 MPa
35000 psi
ISO 178
Flexural Modulus 10.27 GPa
1490 ksi
ISO 178
10.79 GPa
1565 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.76 J/cm
10.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 212 kJ/m²
101 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 2.00 J
1.48 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 39.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 22.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
41.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 22.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 16.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 9.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
16.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 9.06 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 246 °C
475 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
300 °C

@Thickness 3.20 mm
 572 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+6 - 1.00e+8 ohm-cm
1.00e+6 - 1.00e+8 ohm-cm
ASTM D257
Surface Resistance 1.00e+6 - 1.00e+8 ohm
1.00e+6 - 1.00e+8 ohm
ASTM D257