Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6821 BLK This product is based on Kraton G and PP suitable for automotive applications and meets GM, Ford, and Chrysler specifications. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 7318 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 M BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 8002 BLK Multi-Flex® TPE 8002 is based on Shell's Kraton G polymer technology and is widely used in the automotive industry for applications requiring elastomeric performance with excellent ozone resistance.. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 C BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 C GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 C NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 E UV BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 HR BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE A 6221 NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.0345 GPa | 5.00 ksi | ASTM D790 |
Multibase Multi-Flex® A 6221 C TPE Thermoplastic Elastomer Forms: PelletsInformation provided by Multibase |