Polymer Property : Tensile Creep Modulus, 1000 hours = 363000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	2500 - 10000 MPa	363000 - 1.45e+6 psi	Average value: 7610 MPa Grade Count:14
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25..
Tensile Creep Modulus, 1000 hours	2500 - 8300 MPa	363000 - 1.20e+6 psi	Average value: 4360 MPa Grade Count:5
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb..
Tensile Creep Modulus, 1000 hours	2500 MPa	363000 psi	At 1% Deformation; DIN 53444
Wolf Kunststoff ZEDEX® ZX-324V2T A3F PEEK, PTFE Modified Reduced friction; High wear resistance; High elasticity; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automotive Technology; Machine ToolsInformation provided by Zedex
Tensile Creep Modulus, 1000 hours	2500 MPa	363000 psi	elongation <0.5%, 23°C; ISO 899
BASF Ultrason S 2010 PSU Ultrason S 2010 is an unreinforced, medium viscosity standard injection molding PSU grade. It flows readily and offers outstanding heat resistance and dimensional stability. It conforms to FDA req..
Tensile Creep Modulus, 1000 hours	2500 MPa	363000 psi	ISO 899
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
Tensile Creep Modulus, 1000 hours	2500 MPa	363000 psi	ISO 899-1
BASF Ultrason S 3010 PSU Ultrason S 3010 is an unreinforced, higher viscosity injection molding and extrusion PSU grade, tougher and with improved chemical resistance. It conforms to FDA requirements of 21 CFR 177.1655.
Tensile Creep Modulus, 1000 hours	2500 MPa	363000 psi	Elongation <0.5%, 23°C; ISO 899-1
BASF Ultrason S 6010 PSU Ultrason S 6010 is an unreinforced, high molecular weight injection-molding and extrusion grade with excellent chemical resistance (stress crack resistance) and good solubility in typical solvents (..