Polymer Property : Tensile Creep Modulus, 1000 hours = 2200 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	2200 - 2600 MPa	319000 - 377000 psi	Average value: 2450 MPa Grade Count:8
Overview of materials for Polystyrene, Molded, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene". Each property range of values reported is minimum and maximum values of appropriate MatWeb..
Tensile Creep Modulus, 1000 hours	2200 - 3180 MPa	319000 - 461000 psi	Average value: 2520 MPa Grade Count:4
Overview of materials for Nylon 66, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. ..
Tensile Creep Modulus, 1000 hours	2200 MPa @Time 3.60e+6 sec	319000 psi @Time 1000 hour	50%RH; ISO 899-1
DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66 (Unverified Data**) 13% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G13HS1L NC010 is a 13% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Perfor..
Tensile Creep Modulus, 1000 hours	2200 MPa	319000 psi
BASF Polystyrol® 143 E Polystyrene (Europe) Medium strength, easy flowing general-purpose grade, suitable for blending with impact-modified Polystyrol, Styrolux and as a coextruded glossy capping layer.Data was collected by ISO methods and pr..
Tensile Creep Modulus, 1000 hours	2200 MPa	319000 psi
BASF Polystyrol® 144 C Polystyrene (Europe) Very easy flowing grade, often blended with impact-modified Polystyrol or used as a coextruded glossy layer.Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1000 hours	2200 MPa	319000 psi
BASF Polystyrol® 143 EO Polystyrene (Europe) Easy flowing grade for the injection molding and extrusion of low-taint food packaging.Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1000 hours	2200 MPa @Strain <=0.500 %	319000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultradur® B 4300 K6 30% Glass Bead Filled PBT Description: Is a PBT + ASA, Injection-molding grades containing 30% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit..