Polymer Property : Tensile Strength, Ultimate = 79000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	545 MPa @Temperature 200 °C	79000 psi @Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be..
Tensile Strength, Ultimate	545 MPa	79000 psi
Kennametal Stellite StelliteÂ® 3 PM cast Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt..
Tensile Strength, Ultimate	545 MPa @Temperature 870 Â°C	79000 psi @Temperature 1600 Â°F
Haynes Waspaloyâ„¢ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980Â°C (1800Â°F), can be cold-formed in the annealed condition, may also be hot formed at 1040Â°C (1900Â°F) and above, go..
Tensile Strength, Ultimate	545 MPa @Temperature 538 Â°C	79000 psi @Temperature 1000 Â°F
Kennametal Stellite DeloroÂ® N-6 PM with P/M Processing Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data: P/M 17, cast 35. Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing ..
Tensile Strength, Ultimate	545 MPa @Temperature 649 Â°C	79000 psi @Temperature 1200 Â°F
Kennametal Stellite DeloroÂ® N-6 PM with P/M Processing Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data: P/M 17, cast 35. Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing ..
Tensile Strength, Ultimate	545 - 621 MPa	79000 - 90000 psi
Eagle Brass 735 Nickel Silver 18%, Extra Hard 735 is used for coinage, name plates, zippers, flatware, and fashion jewelry.Information provided by Eagle Brass Company
Tensile Strength, Ultimate	545 MPa @Temperature 204 °C	79000 psi @Temperature 399 °F
AK Steel 309S Austenitic Stainless steel AK Steel 309S provides excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures. The alloy is non-magnetic as annealed and becomes slightly magnetic w..
Tensile Strength, Ultimate	545 MPa @Temperature 427 °C	79000 psi @Temperature 801 °F
Carpenter 20Cb-3® Stainless Steel Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re..
Tensile Strength, Ultimate	545 MPa	79000 psi	15% Cold Worked
AK Steel 409 ULTRA FORM® Stainless Steel AK Steel 409 ULTRA FORM Stainless Steel provides an outstanding combination of improved forming and welding characteristics, while providing superior resistance to oxidation, corrosion, ridging and ..
Tensile Strength, Ultimate	545 MPa @Temperature 204 °C	79000 psi @Temperature 399 °F
Carpenter 20-Mo6® Stainless Steel, Tensile Properties at 93°C Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, ..
Tensile Strength, Ultimate	545 MPa	79000 psi	Typical
Aleris Hokotol Aluminum Alloy, 200 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..
Tensile Strength, Ultimate	545 MPa @Temperature 427 °C	79000 psi @Temperature 801 °F
Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1..
Tensile Strength, Ultimate	545 MPa	79000 psi
Carpenter HyMu "80"® Electronic Alloy, Hydrogen Annealed Bar Data provided by Carpenter Technology Corporation.Carpenter HyMu “80” ® alloy is an unoriented, 80% nickel-iron-molybdenum alloy which offers extremely high initial permeability as well as maximu..
Tensile Strength, Ultimate	545 MPa @Temperature 204 °C	79000 psi @Temperature 399 °F
AK Steel 309 Austenitic Stainless steel AK Steel 309 provides excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures. The alloy is non-magnetic as annealed and becomes slightly magnetic wh..