Kennametal Stellite Deloro® N-6 PM with P/M Processing

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Deloro®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Deloro® N-6 PM with P/M Processing.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data: P/M 17, cast 35. Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.19 g/cc
0.296 lb/in³
P/M (98%)
8.48 g/cc
0.306 lb/in³
Theoretical
Mechanical Properties Metric English Comments
Hardness, Brinell 284
284
Converted from Rockwell C hardness.
155

@Temperature 760 °C
 155

@Temperature 1400 °F
 Converted from Rockwell B hardness
228

@Temperature 649 °C
 228

@Temperature 1200 °F
 Converted from Rockwell C hardness
354

@Temperature 538 °C
 354

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Knoop 337
337
Converted from Rockwell C hardness.
179

@Temperature 760 °C
 179

@Temperature 1400 °F
 Converted from Rockwell B hardness
268

@Temperature 649 °C
 268

@Temperature 1200 °F
 Converted from Rockwell C hardness
299

@Temperature 538 °C
 299

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell A 65
65
Converted from Rockwell C hardness.
50

@Temperature 760 °C
 50

@Temperature 1400 °F
 Converted from Rockwell B hardness
60

@Temperature 649 °C
 60

@Temperature 1200 °F
 Converted from Rockwell C hardness
63

@Temperature 538 °C
 63

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell B 105
105
Converted from Rockwell C hardness. Beyond normal Rockwell B range, for comparison only.
82

@Temperature 760 °C
 82

@Temperature 1400 °F
 Hot hardness
98

@Temperature 649 °C
 98

@Temperature 1200 °F
 Converted from Rockwell C hardness
Hardness, Rockwell C 30
30
Hot hardness.
20

@Temperature 649 °C
 20

@Temperature 1200 °F
 Hot hardness.
25

@Temperature 538 °C
 25

@Temperature 1000 °F
 Hot hardness.
Hardness, Vickers 294
294
Converted from Rockwell C hardness.
157

@Temperature 760 °C
 157

@Temperature 1400 °F
 Converted from Rockwell B hardness
234

@Temperature 649 °C
 234

@Temperature 1200 °F
 Converted from Rockwell C hardness
261

@Temperature 538 °C
 261

@Temperature 1000 °F
 Converted from Rockwell C hardness
Tensile Strength, Ultimate 656 MPa
95100 psi
428 MPa

@Temperature 760 °C
 62100 psi

@Temperature 1400 °F
545 MPa

@Temperature 538 °C
 79000 psi

@Temperature 1000 °F
545 MPa

@Temperature 649 °C
 79000 psi

@Temperature 1200 °F
Elongation at Break 2.0 %
2.0 %
in 25.4 mm
3.0 %

@Temperature 538 °C
 3.0 %

@Temperature 1000 °F
 in 25.4 mm
4.0 %

@Temperature 649 °C
 4.0 %

@Temperature 1200 °F
 in 25.4 mm
7.0 %

@Temperature 760 °C
 7.0 %

@Temperature 1400 °F
 in 25.4 mm
Modulus of Elasticity 200 GPa
29000 ksi
Component Elements Properties Metric English Comments
Boron, B 0.60 %
0.60 %
Carbon, C 1.1 %
1.1 %
Chromium, Cr 29 %
29 %
Cobalt, Co <= 3.0 %
<= 3.0 %
Iron, Fe <= 3.0 %
<= 3.0 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Molybdenum, Mo 5.5 %
5.5 %
Nickel, Ni 54 %
54 %
As Remainder
Silicon, Si <= 1.5 %
<= 1.5 %
Tungsten, W 2.0 %
2.0 %