Kennametal Stellite Stellite® 3 PM cast

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Stellite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Stellite® 3 PM cast.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Adhesive wear test data: P/M 0.10, Cast 0.24. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.64 g/cc
0.312 lb/in³
theoretical
Mechanical Properties Metric English Comments
Hardness, Brinell 533
533
Converted from Rockwell C hardness.
265

@Temperature 760 °C
265

@Temperature 1400 °F
Converted from Rockwell C hardness
345

@Temperature 649 °C
345

@Temperature 1200 °F
Converted from Rockwell C hardness
415

@Temperature 538 °C
415

@Temperature 1000 °F
Converted from Rockwell C hardness
Hardness, Knoop 643
643
Converted from Rockwell C hardness.
313

@Temperature 760 °C
313

@Temperature 1400 °F
Converted from Rockwell C hardness
413

@Temperature 649 °C
413

@Temperature 1200 °F
Converted from Rockwell C hardness
499

@Temperature 538 °C
499

@Temperature 1000 °F
Converted from Rockwell C hardness
Hardness, Rockwell A 77
77
Converted from Rockwell C hardness.
64

@Temperature 760 °C
64

@Temperature 1400 °F
Converted from Rockwell C hardness
69

@Temperature 649 °C
69

@Temperature 1200 °F
Converted from Rockwell C hardness
73

@Temperature 538 °C
73

@Temperature 1000 °F
Converted from Rockwell C hardness
Hardness, Rockwell C 54
54
Hot hardness.
27

@Temperature 760 °C
27

@Temperature 1400 °F
Hot hardness.
38

@Temperature 649 °C
38

@Temperature 1200 °F
Hot hardness.
45

@Temperature 538 °C
45

@Temperature 1000 °F
Hot hardness.
Hardness, Vickers 575
575
Converted from Rockwell C hardness.
274

@Temperature 760 °C
274

@Temperature 1400 °F
Converted from Rockwell C hardness
362

@Temperature 649 °C
362

@Temperature 1200 °F
Converted from Rockwell C hardness
441

@Temperature 538 °C
441

@Temperature 1000 °F
Converted from Rockwell C hardness
Tensile Strength, Ultimate 545 MPa
79000 psi
483 MPa

@Temperature 649 °C
70100 psi

@Temperature 1200 °F
483 MPa

@Temperature 760 °C
70100 psi

@Temperature 1400 °F
497 MPa

@Temperature 538 °C
72100 psi

@Temperature 1000 °F
Elongation at Break <= 1.0 %
<= 1.0 %
in 25.4 mm
Thermal Properties Metric English Comments
CTE, linear 12.3 µm/m-°C

@Temperature 0.000 - 100 °C
6.83 µin/in-°F

@Temperature 32.0 - 212 °F
12.5 µm/m-°C

@Temperature 0.000 - 200 °C
6.94 µin/in-°F

@Temperature 32.0 - 392 °F
12.7 µm/m-°C

@Temperature 0.000 - 300 °C
7.06 µin/in-°F

@Temperature 32.0 - 572 °F
12.9 µm/m-°C

@Temperature 0.000 - 400 °C
7.17 µin/in-°F

@Temperature 32.0 - 752 °F
13.0 µm/m-°C

@Temperature 0.000 - 500 °C
7.22 µin/in-°F

@Temperature 32.0 - 932 °F
13.1 µm/m-°C

@Temperature 0.000 - 600 °C
7.28 µin/in-°F

@Temperature 32.0 - 1110 °F
13.4 µm/m-°C

@Temperature 0.000 - 700 °C
7.44 µin/in-°F

@Temperature 32.0 - 1290 °F
13.7 µm/m-°C

@Temperature 0.000 - 800 °C
7.61 µin/in-°F

@Temperature 32.0 - 1470 °F
14.5 µm/m-°C

@Temperature 0.000 - 900 °C
8.06 µin/in-°F

@Temperature 32.0 - 1650 °F
16.0 µm/m-°C

@Temperature 0.000 - 1000 °C
8.89 µin/in-°F

@Temperature 32.0 - 1830 °F
Melting Point 1213 - 1285 °C
2215 - 2345 °F
Solidus 1213 °C
2215 °F
Liquidus 1285 °C
2345 °F
Component Elements Properties Metric English Comments
Boron, B <= 1.0 %
<= 1.0 %
Carbon, C 2.4 %
2.4 %
Chromium, Cr 31 %
31 %
Cobalt, Co 44 %
44 %
As remainder
Iron, Fe <= 3.0 %
<= 3.0 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Nickel, Ni <= 3.0 %
<= 3.0 %
Other <= 1.0 %
<= 1.0 %
Silicon, Si <= 1.0 %
<= 1.0 %
Tungsten, W 12.5 %
12.5 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.20

@Temperature 22.0 °C
<= 1.20

@Temperature 71.6 °F
200 Oersted