Polymer Property : Tensile Strength, Ultimate = 780 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	780 MPa @Temperature 540 Â°C	113000 psi @Temperature 1000 Â°F
Haynes 25 alloy, hot rolled and 1230Â°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	780 MPa	113000 psi
Haynes 556Â® alloy, bar, after 0 hours at 650Â°C (1200Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	780 MPa	113000 psi
Haynes 556Â® alloy, bar, after 1000 hours at 870Â°C (1600Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	780 MPa	113000 psi
Haynes HastelloyÂ® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Ultimate	780 - 840 MPa	113000 - 122000 psi
CLAL-MSX DECLAFOR® 1015 TH1 Rod quenched/Cold Rolled/Precipitation Heat Treated Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn..
Tensile Strength, Ultimate	780 - 880 MPa	113000 - 128000 psi
CLAL-MSX NICLAFOR® 1000 TD4 Quenched/Cold Rolled, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate	>= 780 MPa	>= 113000 psi
CLAL-MSX NICLAFOR® 1000 TDX Quenched/Cold Rolled, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal Complex Phase Steel 800 Y500 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT780C) and electrogalvanized (HCT780C+ZE)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product r..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal Complex Phase Steel 800 Y600 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT780C), electrogalvanized (HCT780C+ZE) and Extragal®/Galvannealed (HCT780+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS ..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal Dual Phase 780 LCE Y450 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal Dual Phase 780 LCE Y500 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal TRIP 780 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT780T), electrogalvanized (HCT780T+ZE) and Extragal®/Galvannealed (HCT780T+Z/+ZZF)Description: TRIP steels offer an outstanding combination of strength and d..
Tensile Strength, Ultimate	>= 780 MPa	>= 113000 psi
ArcelorMittal Complex Phase Steel 800 Very high strength steel, Hot Rolled Steel Available in the following: uncoated (HCT780C) and Extragal®/Galvannealed (HCT780C+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) prod..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal Dual Phase 780 Y450 Very high strength steel, Cold Rolled Steel Available in the following: HCT780X (uncoated), HCT780X+ZE (electrogalvanized) and HCT780X+Z/ZF (Extragal®/Galvannealed)Description: Dual Phase steels offer an outstanding combination of strength a..
Tensile Strength, Ultimate	780 - 900 MPa	113000 - 131000 psi
ArcelorMittal Dual Phase 780 Y500 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..