Polymer Property : Tensile Strength, Ultimate = 6.20 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	6.20 MPa	899 psi	ASTM D412
Multibase Multi-Flex® TPE A 7521 BLK Ash is 36%. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	6.20 MPa	899 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 812P Polyethylene (discontinued **) Polyethylene 812A is a natural low density material with a 200 melt index. Its high melt index exhibits excellent wettability. This makes it ideal as a carpet backing to bind fibers to the carpet...
Tensile Strength, Ultimate	6.20 MPa	899 psi	ASTM D638
ExxonMobil Escorene® LD-781 High EVA Compounding Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 33% vinyl acetate copolymer for specialty compounding applications. The resin provides excellent stress cracking and flexibility, and allows outs..
Tensile Strength, Ultimate	>= 6.20 MPa	>= 899 psi
Arlon 0.015" (0.381 mm) Semi-Cured Silicone Traction Motor Insulation with Fiberglass Substrate (51224R015) &n 0.007 in. (0.18 mm) nominal semi-cured silicone rubber on 0.008 in. (0.2 mm) Prime Coated 7628 Fiberglass; 0.003 in. (0.8 mm) polyethylene interleave; overall thickness 0.015 in. ± 0.0015 (0.038 mm..
Tensile Strength, Ultimate	6.20 MPa	899 psi	GB/T 528
Chengdu Polyster FR2075 Flame Retardant Grade TPV Good heat stability and light stability. Meets the requirements of European Dioxine Principle and the environmental protection criteria. Can be used for wires, cables, buncles, carcass of train.Inf..
Tensile Strength, Ultimate	6.20 MPa	899 psi
Dow Corning SILASTIC® LSR 9390-50 PARTS A&B 50 Durometer, 2-part, 1 to 1 mix, off-white, injection molding grade, Liquid Silicone RubberInformation provided by Dow Corning
Tensile Strength, Ultimate	6.20 MPa	899 psi
Dow Primacor® 5990I Ethylene Acrylic Acid (EAA) PRIMACOR® 5990I is an ethylene acrylic acid copolymer (20 wt % comonomer) for specialty hot melt adhesive applications. Its outstanding properties include toughness and adhesion to a wide variety o..
Tensile Strength, Ultimate	>= 6.20 MPa	>= 899 psi
Arlon 0.011" (0.2794 mm) Uncured Silicone Traction Motor Insulation (P29600R011) 0.006 in., +0.002, -0.001(0.2 mm, +0.05, -0.03) uncured silicone on 0.005 in. (0.08 mm) nominal PTFE coated fiberglass; 0.0015 in. (0.038 mm) polyethylene interleave; overall thickness 0.011 in ±0...
Tensile Strength, Ultimate	>= 6.20 MPa	>= 899 psi
Arlon 0.020" (0.508 mm) Layer-on-Layer Silicone Traction Motor Insulation (P29609R020) 0.010 in. (0.25 mm) minimum uncured silicone on 0.002 in. (0.5 mm) minimum cured silicone on 0.008 in. (0.2 mm) nominal Prime Coated 7628 Fiberglass; 0.0015 in. (0.038 mm) polyethylene interleave; o..
Tensile Strength, Ultimate	6.20 MPa @Thickness 1.14 - 1.52 mm, Temperature 816 °C	899 psi @Thickness 0.0449 - 0.0598 in, Temperature 1500 °F
AK Steel 409 Ferritic Stainless steel AK Steel 409 Stainless Steels are especially useful for applications where oxidation or corrosion protection beyond the capacity of carbon steel and some coated steels is needed. Current applicatio..
Tensile Strength, Ultimate	6.20 MPa	899 psi	TPE-0153 (ASTM D 412)
ExxonMobil Vyram™ 9271-75 Thermoplastic Rubber (discontinued **) A colorable thermoplastic elastomer which complies with FDA regulations for rubber articles intended for repeated use, as well as rubber articles in contact with non-fatty, non-oily foods as closure..