Arlon 0.015" (0.381 mm) Semi-Cured Silicone Traction Motor Insulation with Fiberglass Substrate (51224R015) &n

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Silicone
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 0.015" (0.381 mm) Semi-Cured Silicone Traction Motor Insulation with Fiberglass Substrate (51224R015) &n.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
0.007 in. (0.18 mm) nominal semi-cured silicone rubber on 0.008 in. (0.2 mm) Prime Coated 7628 Fiberglass; 0.003 in. (0.8 mm) polyethylene interleave; overall thickness 0.015 in. ± 0.0015 (0.038 mm ±0.0038). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 566.2 g/m² ± 1.5 (16.7 oz./yd.² ± 1.5). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours. Flame Test Method: FTMS 191A, Method 5903. Maximum Flame and Glow Time: 15 seconds. Maximum Char Length: 7.62 cm (3 in).Information provided by the manufacturer, Arlon Silicone Technologies Division.
Mechanical Properties Metric English Comments
Hardness, Shore A 55 - 65
55 - 65
Tensile Strength, Ultimate >= 6.20 MPa
>= 899 psi
Elongation at Break >= 200 %
>= 200 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.6 °C
-69.9 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.75 kV/mm
>= 400.0 kV/in
Processing Properties Metric English Comments
Processing Temperature 176.6 °C
349.9 °F