Arlon 0.020" (0.508 mm) Layer-on-Layer Silicone Traction Motor Insulation (P29609R020)

Category	Polymer , Thermoset , Silicone
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 0.020" (0.508 mm) Layer-on-Layer Silicone Traction Motor Insulation (P29609R020).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

0.010 in. (0.25 mm) minimum uncured silicone on 0.002 in. (0.5 mm) minimum cured silicone on 0.008 in. (0.2 mm) nominal Prime Coated 7628 Fiberglass; 0.0015 in. (0.038 mm) polyethylene interleave; overall thickness 0.020 in ± 0.001 (0.51 mm ± 0.03). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 627.3 g/m² ± 67.8 (18.5 oz./yd.² ± 2.0). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours.Information provided by the manufacturer, Arlon Silicone Technologies Division.

Mechanical Properties	Metric	English
Hardness, Shore A	55 - 65	55 - 65
Tensile Strength, Ultimate	>= 6.20 MPa	>= 899 psi
Elongation at Break	>= 200 %	>= 200 %

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	260 °C	500 °F
Minimum Service Temperature, Air	-56.6 °C	-69.9 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.75 kV/mm	>= 400.0 kV/in

Processing Properties	Metric	English	Comments
Processing Temperature	176.6 °C	349.9 °F	curing temp., at 0.345 MPa (50 psi)