Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 420 MPa @Temperature 200 °C |
60900 psi @Temperature 392 °F |
EN min.; EN 10002-5 |
Outokumpu 4432 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
Tensile Strength, Ultimate | 420 MPa @Temperature 100 °C |
60900 psi @Temperature 212 °F |
EN min.; EN 10002-5 |
Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
Tensile Strength, Ultimate | 420 MPa @Temperature 870 °C |
60900 psi @Temperature 1600 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
Tensile Strength, Ultimate | 420 - 490 MPa | 60900 - 71100 psi | |
SSAB Tunnplat Aluzink 350A YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Aluzink YP - HSLA steel (aluminum-zinc coated sheet). Property values are for thicknesses 0.4 - 2.0 mm. Iron content is approximate - exact composition is .. |
|||
Tensile Strength, Ultimate | <= 420 MPa | <= 60900 psi | |
SSAB Tunnplat Aluzink B420A Metal-coated Mild Steel Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu.. |
|||
Tensile Strength, Ultimate | <= 420 MPa | <= 60900 psi | |
SSAB Tunnplat Aluzink F26A Metal-coated Mild Steel Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu.. |
|||
Tensile Strength, Ultimate | 420 - 500 MPa | 60900 - 72500 psi | |
SSAB Tunnplat Docol® 300 BH High-strength Steel High-strength SteelComments: Docol BH - Cold Rolled Steel - rephosphorized steel with bake hardening effect. Property values are for cold-rolled steel; thicknesses 0.40 - 2.0 mm. Iron content is ap.. |
|||
Tensile Strength, Ultimate | 420 - 500 MPa | 60900 - 72500 psi | |
SSAB Tunnplat Docol® 300 RP High-strength Steel High-strength SteelComments: Docol RP - Cold Rolled Steel - rephosphorized steel. Property values are for cold-rolled steel; thicknesses 0.40 - 3.0 mm. Iron content is approximate - exact compositi.. |
|||
Tensile Strength, Ultimate | 420 - 490 MPa | 60900 - 71100 psi | |
SSAB Tunnplat Dogal 350YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Dogal YP - HSLA steel. Property values are for thicknesses 0.4 to 2.5 mm. Iron content is approximate - exact composition is not reported by the manufactur.. |
|||
Tensile Strength, Ultimate | <= 420 MPa | <= 60900 psi | |
SSAB Tunnplat Dogal B420 Metal-coated Mild Steel Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac.. |
|||
Tensile Strength, Ultimate | <= 420 MPa | <= 60900 psi | |
SSAB Tunnplat Dogal F26 Metal-coated Mild Steel Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac.. |
|||
Tensile Strength, Ultimate | >= 420 MPa | >= 60900 psi | |
SSAB Tunnplat Domex® 350XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. Gene.. |
|||
Tensile Strength, Ultimate | >= 420 MPa | >= 60900 psi | |
SSAB Tunnplat Domex® 350YP Cold-forming Steel, HSLA Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. General use of Domex®.. |
|||
Tensile Strength, Ultimate | 420 MPa | 60900 psi | |
Wieland 1023 Wilaform Gold Hard yellow gold alloy with good extensibility. Particularly suitable for by machine manufactured decoration.Applications: casting, chains, coin/shape, laminar decorationDental |
|||
Tensile Strength, Ultimate | 420 MPa | 60900 psi | |
Wieland 1101 Wilaform Gold Hard yellow gold alloy with good extensibility. Universally applicable in decoration manufacturing.Applications: casting, chainsDental |
|||
Tensile Strength, Ultimate | <= 420 MPa | <= 60900 psi | Wire |
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. Its machineability is one of the best of all of the corrosion resistant alloys. The very good machineability of.. |
|||
Tensile Strength, Ultimate | 420 - 500 MPa | 60900 - 72500 psi | |
CLAL-MSX NICLAFOR® 1000 TB Quenched Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
Tensile Strength, Ultimate | 420 - 480 MPa | 60900 - 69600 psi | Wire |
CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 420 - 480 MPa | 60900 - 69600 psi | |
ArcelorMittal 300 BH Bake hardening steel, Cold rolled Available in the following: uncoated (HC300B), electroglavanized (HC300B+ZE) and Extragal®/Galvannealed (HC300BD+Z)Description: The composition and processing of these steels are designed to promot.. |
|||
Tensile Strength, Ultimate | 420 - 490 MPa | 60900 - 71100 psi | |
ArcelorMittal HSLA 340 High strength low alloy steel for cold forming, Cold Rolled Available in the following: uncoated (HC340LA), electroglavanized (HC340LA +ZE) and Extragal®/galfan/Galvannealed (HC340LA+Z/+ZA/+ZF)Description: Steels in the HSLA (High Strength Low Alloy) range .. |