Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
RT
Mechanical Properties Metric English Comments
Hardness, Brinell 150
150
Outokumpu Typical, 20°C, Hot rolled plate (Quarto)/Cold rolled strip/sheet; EN 10003-1
Tensile Strength, Ultimate 570 MPa
82700 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
370 MPa

@Temperature 300 °C
53700 psi

@Temperature 572 °F
EN min.; EN 10002-5
380 MPa

@Temperature 200 °C
55100 psi

@Temperature 392 °F
EN min.; EN 10002-5
420 MPa

@Temperature 100 °C
60900 psi

@Temperature 212 °F
EN min.; EN 10002-5
840 MPa

@Temperature -80.0 °C
122000 psi

@Temperature -112 °F
EN min; EN 10002-5
1200 MPa

@Temperature -196 °C
174000 psi

@Temperature -321 °F
EN min; EN 10002-5
Tensile Strength, Yield 220 MPa

@Strain 0.200 %
31900 psi

@Strain 0.200 %
EN min.,RT; EN 10002-1
270 MPa

@Strain 0.200 %
39200 psi

@Strain 0.200 %
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
310 MPa

@Strain 1.00 %
45000 psi

@Strain 1.00 %
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
100 MPa

@Strain 0.200 %,
Temperature 500 °C
14500 psi

@Strain 0.200 %,
Temperature 932 °F
EN min.; EN 10002-5
108 MPa

@Strain 0.200 %,
Temperature 400 °C
15700 psi

@Strain 0.200 %,
Temperature 752 °F
EN min.; EN 10002-5
119 MPa

@Strain 0.200 %,
Temperature 300 °C
17300 psi

@Strain 0.200 %,
Temperature 572 °F
EN min.; EN 10002-5
128 MPa

@Strain 1.00 %,
Temperature 500 °C
18600 psi

@Strain 1.00 %,
Temperature 932 °F
EN min.; EN 10002-5
135 MPa

@Strain 1.00 %,
Temperature 400 °C
19600 psi

@Strain 1.00 %,
Temperature 752 °F
EN min.; EN 10002-5
137 MPa

@Strain 0.200 %,
Temperature 200 °C
19900 psi

@Strain 0.200 %,
Temperature 392 °F
EN min.; EN 10002-5
145 MPa

@Strain 1.00 %,
Temperature 300 °C
21000 psi

@Strain 1.00 %,
Temperature 572 °F
EN min.; EN 10002-5
165 MPa

@Strain 0.200 %,
Temperature 100 °C
23900 psi

@Strain 0.200 %,
Temperature 212 °F
EN min.; EN 10002-5
165 MPa

@Strain 1.00 %,
Temperature 200 °C
23900 psi

@Strain 1.00 %,
Temperature 392 °F
EN min.; EN 10002-5
200 MPa

@Strain 1.00 %,
Temperature 100 °C
29000 psi

@Strain 1.00 %,
Temperature 212 °F
EN min.; EN 10002-5
275 MPa

@Strain 0.200 %,
Temperature -80.0 °C
39900 psi

@Strain 0.200 %,
Temperature -112 °F
EN min.; EN 10002-5
350 MPa

@Strain 0.200 %,
Temperature -196 °C
50800 psi

@Strain 0.200 %,
Temperature -321 °F
EN min.; EN 10002-5
355 MPa

@Strain 1.00 %,
Temperature -80.0 °C
51500 psi

@Strain 1.00 %,
Temperature -112 °F
EN min.; EN 10002-5
450 MPa

@Strain 1.00 %,
Temperature -196 °C
65300 psi

@Strain 1.00 %,
Temperature -321 °F
EN min.; EN 10002-5
Elongation at Break 55 %
55 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
35 %

@Temperature -196 °C
35 %

@Temperature -321 °F
EN min
40 %

@Temperature -80.0 °C
40 %

@Temperature -112 °F
EN min
Modulus of Elasticity 200 GPa
29000 ksi
RT
165 GPa

@Temperature 500 °C
23900 ksi

@Temperature 932 °F
172 GPa

@Temperature 400 °C
24900 ksi

@Temperature 752 °F
179 GPa

@Temperature 300 °C
26000 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Cold rolled strip/sheet, 10x10mm test pieces; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 100 °C
8.89 µin/in-°F

@Temperature 212 °F
17.5 µm/m-°C

@Temperature 400 °C
9.72 µin/in-°F

@Temperature 752 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
20.0 W/m-K

@Temperature 400 °C
139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 17.3 %
17.3 %
Iron, Fe 67.48 %
67.48 %
Molybdenum, Mo 2.6 %
2.6 %
Nickel, Ni 12.6 %
12.6 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000750 ohm-cm
0.0000750 ohm-cm
RT