Polymer Property : Tensile Strength, Ultimate = 2990 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	20.6 MPa	2990 psi	ASTM D412-80
DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerato..
Tensile Strength, Ultimate	20.6 MPa @Thickness 3.17 mm	2990 psi @Thickness 0.125 in	Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638
NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, ..
Tensile Strength, Ultimate	20.6 MPa @Thickness 3.17 mm	2990 psi @Thickness 0.125 in	Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638
NOVA Chemicals Novapol® TR-0338-UIG Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, ..
Tensile Strength, Ultimate	20.6 MPa	2990 psi	ISO 37
Kuraray SEPTONÂ® S8007 Thermoplastic Rubber SEPTONÂ® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTONÂ® resins are hydrogenated styrenic block copolymers, which exhi..
Tensile Strength, Ultimate	>= 20.6 MPa @Temperature 100 Â°C	>= 2990 psi @Temperature 212 Â°F
Sibur SKI-3 1st Grade, 1st Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment.
Tensile Strength, Ultimate	>= 20.6 MPa @Temperature 100 Â°C	>= 2990 psi @Temperature 212 Â°F
Sibur SKI-3 Superior Quality, 3rd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment.
Tensile Strength, Ultimate	>= 20.6 MPa @Temperature 100 Â°C	>= 2990 psi @Temperature 212 Â°F
Sibur SKI-3S 1st Grade, 1st Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. It is used instead of natural rubber during production of colored rubber articles, medical articles, and rubbers contacting with food products.
Tensile Strength, Ultimate	>= 20.6 MPa @Temperature 100 Â°C	>= 2990 psi @Temperature 212 Â°F
Sibur SKI-3S 1st Grade, 2nd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. It is used instead of natural rubber during production of colored rubber articles, medical articles, and rubbers contacting with food products.
Tensile Strength, Ultimate	20.6 MPa	2990 psi	ASTM D638
SK Chemicals SKYPEL P147D Productivity Grade SKYPEL is a thermoplastic polyester elastomer (TPEE). It is a polymer resin having the property somewhere between plastics and rubber, which have various properties ranging from high hardness plasti..
Tensile Strength, Ultimate	20.6 MPa	2990 psi	ASTM D638
Samyang TrielÂ® 5450 Thermoplastics Polyetherester Elastomer, General Extrusion Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5450 is an extrusion grade.Information provided by Samyang.
Tensile Strength, Ultimate	<= 20.6 MPa	<= 2990 psi	With carbon black or gum stocks. ASTM D412-80
DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, General Description (discontinu Product form is white, odorless chips. Distinguishing Feature: Readily soluble in common solvents. Good low temperature flexibility.29 % Chlorine Content. 1.4% Sulfur Content. Very Good Abrasion..