Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 450 MPa @Diameter 55.0 - 100 mm |
65300 psi @Diameter 2.17 - 3.94 in |
|
United Cast Bar Unibar 500-7 Continuously Cast Spheroidal Graphite Iron Offers higher wear resistance, strength & heat-treatment response while still possessing good machinability and excellent surface finishes. Noise and vibration damping are good in this grade.Unibar .. |
|||
Tensile Strength | 450 MPa @Thickness 15.0 - 38.1 mm |
65300 psi @Thickness 0.591 - 1.50 in |
Typical Strength |
Constellium Alumold® 400 Aluminum The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds.. |
|||
Tensile Strength | >= 450 MPa @Thickness 300 - 400 mm |
>= 65300 psi @Thickness 11.8 - 15.7 in |
long-transverse direction |
Constellium Alumold® 500 Forged Aluminum Forged thick blocks in Alumold® 500 have been developed to provide high and consistent strength across the thickness, good dimensional stability and excellent machinability, in order to respond to .. |
|||
Tensile Strength | 450 MPa @Thickness 400 - 450 mm |
65300 psi @Thickness 15.7 - 17.7 in |
long-transverse direction |
Constellium Alumold® 500 Forged Aluminum Forged thick blocks in Alumold® 500 have been developed to provide high and consistent strength across the thickness, good dimensional stability and excellent machinability, in order to respond to .. |
|||
Tensile Strength | >= 450 MPa @Thickness 325 - 400 mm |
>= 65300 psi @Thickness 12.8 - 15.7 in |
Temper T652 |
Constellium Certal® SPC Forged Aluminum Certal® SPC forged has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property.. |
|||
Tensile Strength | >= 450 MPa @Thickness 180 - 200 mm |
>= 65300 psi @Thickness 7.09 - 7.87 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |